Large Magnetocaloric Effect in Li 3 K 9 Gd 3 (BO 3 ) 7 Crystal Featuring Sandwich-Like Three-Dimensional Framework

Wang Liu,Fei Liang,Yuwei Chen,Huimin Song,Jingcheng Feng,Jun Shen,Zheshuai Lin,Heng Tu,Guochun Zhang

DOI: https://doi.org/10.1021/acs.inorgchem.1c00633

IF: 4.6

2021-04-12

Inorganic Chemistry

Abstract:A new Gd-based borate crystal, Li₃K₉Gd₃(BO₃)₇, has been successfully obtained via the high-temperature solution method using Li₂O-K₂O-B₂O₃ self-flux. It crystallizes in monoclinic space group <i>P</i>2/<i>n</i> (no. 10) with lattice parameters <i>a</i> = 11.3454(6) Å, <i>b</i> = 9.9881(4) Å, <i>c</i> = 11.4467(7) Å, α = γ = 90 ^o, β = 114.782(7) ^o, and <i>Z</i> = 2. Li₃K₉Gd₃(BO₃)₇ exhibits an intriguing sandwich-like three-dimensional (3D) framework constructed from [Gd-B-O]_∞ layers, KO_<i>n</i> (<i>n</i> = 6 and 8) polyhedra, and LiO₄ tetrahedra, in which [Gd-B-O]_∞ layers are built from two types of GdO₈ polyhedra and triangular BO₃ units. Magnetic measurements showed that Li₃K₉Gd₃(BO₃)₇ exhibits a large magnetocaloric effect with -Δ<i>S</i>_<i>m</i> = 39.3 J kg^-1 K^-1 at 2.0 K for Δ<i>H</i> = 7 T, which is slightly higher than that of the commercial gadolinium gallium garnet under the same conditions. The powder X-ray diffraction, infrared spectrum, and UV-vis-NIR diffuse reflectance spectrum were also performed to characterize Li₃K₉Gd₃(BO₃)₇. The electronic band structures, partial density of states, and refractive indices of Li₃K₉Gd₃(BO₃)₇ were investigated via the first-principle calculations.

chemistry, inorganic & nuclear