O,N-Codoped CeF 3 Upconversion Nanoparticles for Efficient Photocatalytic Oxygen Evolution under Visible Light
Bing Han,Yunchao Lou,Zhe Liu,Chutong Zhou,Zhiyu Wang,Guodong Qian
DOI: https://doi.org/10.1021/acsanm.2c00140
IF: 6.14
2022-03-30
ACS Applied Nano Materials
Abstract:Visible light response is as important as energy band potential for photocatalytic water splitting. In this work, upconversion CeF3 nanoparticles are developed by O and N doping. The contents and species of O and N regulated by various temperatures act on the large-scale regulation of defects and band structures distinctly, which can suppress the recombination of photogenerated carriers. O,N-CeF3-160 nanoparticles establish the most suitable defects and electronic structure in all O,N-CeF3 nanoparticles. It exhibits the optimal oxygen evolution rates up to 1277 μmol g–1 h–1, whose apparent quantum yield (AQY) is up to 53.09% at 550 nm. The photoluminescence (PL) spectra and density of state (DOS) illustration elucidate the internal reason for the distinct photocatalysis activity. Defects are just as important as band structure in the modification of O,N-codoped CeF3 upconversion nanoparticles. This work provides the approach to regulate CeF3 upconversion materials to achieve better photoactivity under visible light.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsanm.2c00140.TEM images of the precursor (Figure S1); XPS of survey, Ce 3d, and F 1s (Figure S2); the photocurrent responses for O,N-CeF3 nanoparticles (Figure S3); UV–vis spectra of pure CeF3 and O,N-CeF3 nanoparticles (Figure S4); quantification of Ce, F, O, and N signals for O,N-CeF3 nanoparticles (Table S1); quantification of O and N signals for O,N-CeF3 nanoparticles (Table S2); the AQY of recently reported other OER photocatalysts (Table S3); lifetime fitting data for O,N-CeF3 nanoparticles and pure CeF3 (Table S4); the calculated band structures of O,N-CeF3 nanoparticles (Table S5); and Supporting Information references (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology