Preparation and in vitro compatibility of transforming growth factor beta 1 loaded chitosan microspheres
Si Chen,Nian-guo Dong,Jia-wei Shi,Chao Guo,Hong-xu Qi
DOI: https://doi.org/10.3321/j.issn:1673-8225.2008.32.016
2008-01-01
Abstract:Background: Releasing growth factor through controlled release system is one of the study directions of bioactive factor application. Objective: To prepare transforming growth factor β1 (TGF-β 1) loaded chitosan microspheres with ionically cross-linking precipitant method, and to study the properties of controlled release of TGF-β 1 and biocompatibility in vitro. Design, time and setting: An observational trial was performed in the central labotatory, Union Hospital, Tongji Medical College, Huazhong University of Science and Technology (Wuhan, Hubei, China) from October 2006 to September 2007. Materials: Chitosan, 90% deacetylation degree, was offered by Tsinghua University Chemical Engineering Department; TGF-β 1 was offered by Jingmei Biotech Co., Ltd.; Rats were offered by the Experimental Animal Center of Tongji Medical College, Huazhong University of Science and Technology. Methods: Chitosan microspheres were prepared with ionically cross-linking precipitant method, and TGF-β 1 was then packaged in the microspheres. After passage culture, myofibroblasts in descending thoracic aorta of rats at the adjusted concentration of 1× 10 8/L were added with chitosam microsphere leaching liquor (4, 2, 1 g/L), while the medium without leaching liquor was taken as controls. Main outcome measures: The features such as the size distribution, drug content, drug encapsulating and in vitro release were studied with scanning electron microscope, laser grainsize analyzer and ELISA method. MTT test was performed to observe cell proliferation and evaluate the biocompatibility in vitro. Results: The microspheres were spherical and smooth. The mean diameters of the spheres were 272 nm, and the high encapsulation efficiency was obtained, about 80.6%. The sudden release of TGF-β 1 was observed in the initial period in test of release in vitro, and then TGF-β 1 could be constantly released from the chitosan microspheres (27% in 24 hours and up to 41% in 7 days). MTT showed that the chitosan microspheres did not damage the cell growth in vitro, indicating good compatibility. Conclusion: The method to prepare chitosan microspherea with ionically cross-linking precipitant is convenient and feasible, and TGF-β 1 possesses good delayed release and compatibility.