Shape-controlled synthesis of Pt3Co nanocrystals with high electrocatalytic activity toward oxygen reduction.
Sang‐Il Choi,Ran Choi,S. Han,Joon-Taik Park
DOI: https://doi.org/10.1002/chem.201101138
2011-10-24
Chemistry
Abstract:Polymer electrolyte membrane fuel cells (PEMFCs), a promising alternative energy system, have been intensively explored as a power source for electric vehicles or appliances. Since their performance is limited by the slow reduction kinetics of the oxygen reduction reaction (ORR) at the cathode, improving the ORR activity is key to developing efficient PEMFCs. For this reason, the synthesis of Pt alloy nanoparticles with controlled compositions and morphologies has been extensively exploited for the last decade. Previous studies revealed that the ORR activities of Pt–M (where M is Co, Ni, Fe, Mn, Cr, Cu, and Pd) alloys are superior to those of pure Pt catalysts. In addition, their ORR kinetics can be controlled by tuning their morphologies because the enhancement of the ORR activity depends highly on the surface atom arrangements of the catalyst particles. For example, Pt3Mn nanocubes dominantly bound by {100} planes exhibited ORR activity that was three-times higher than that of the commercial Pt/C catalyst in H2SO4 media. [11] However, investigations of catalysts based on the Pt3Ni octahedra and truncated octahedra in HClO4 have shown that the catalytic activity is higher on the Pt3Ni {111} planes than that on the {100} planes because the trend of binding the sulfate anions on the {111} planes is not established in this media. In addition, Stamenkovic et al. demonstrated that the catalytic activity is determined by the low coverage of OHad, and that the ORR on Pt3Ni {111} planes is the highest among the low-index planes. The Pt–Co alloy nanoparticles have drawn particular interest as ORR electrocatalysts due to their enhanced catalytic activities, which can be attributed to the modified electronic structure of Pt, the tuned strength of the oxygen– metal bonding, and the low toxicity of dissolved Co ions against the polymer electrolyte. Although it might be possible to modulate the catalytic properties of Pt–Co nanoparticles by controlling their morphologies, the shapecontrolled synthesis of Pt–Co nanoparticles and their morphology-dependent ORR activities have rarely been reported. Recently, we have demonstrated that the Pt9Co alloy nanocubes bound by {100} planes show a fourfold improvement of catalytic activity toward ORR over the commercial Pt/C catalyst in an H2SO4 solution. [18] Herein, we describe the synthesis of Pt3Co nanocubes (NCs) and nanotruncated octahedra (NTO), the surfaces of which are dominated by {100} and {111}/ ACHTUNGTRENNUNG{100} planes, respectively. The selective synthesis of Pt3Co NCs and NTO was achieved by controlling the reaction time. The prepared Pt3Co NTO exhibited significantly enhanced ORR activity compared to the Pt3Co NCs and commercial Pt/C catalyst. In a typical synthesis of Pt3Co nanocrystals, Pt ACHTUNGTRENNUNG(acac)2 (acac=acetylacetonate) and Co2(CO)8, in a molar ratio of 2:1 were employed as precursors, and oleylamine (OAm) and oleic acid (OA) were used as surfactants. The Pt3Co NTO and Pt3Co NCs were selectively obtained as black– brown nanocrystals by heat treatment from 120 to 200 8C for 30 min, with a temperature increase rate of 2–3 8C min , and incubation at 200 8C for 30 min for Pt3Co NTO and 90 min for Pt3Co NCs under identical experimental conditions (see the Experimental Section). The resultant Pt3Co nanocrystals were readily dispersed in organic solvents, such as toluene and hexane. The transmission electron microscopy (TEM) images of the as-synthesized Pt3Co NCs and NTO, with an average size of 8 nm, indicate the selective formation of NCs and NTO with good uniformity (Figure 1 a and 1 c, respectively). Figure 1 b and 1 d shows high-resolution TEM (HRTEM) images of a single Pt3Co NC and NTO, respectively.