Cu/CuxO@C nanocomposites as efficient electrodes for high-performance supercapacitor devices
Yuxuan Guo,Changyun Chen,Yumeng Wang,Ye Hong,Kuaibing Wang,Dongdong Niu,Cheng Zhang,Qichun Zhang
DOI: https://doi.org/10.1039/d2dt02268k
IF: 4
2022-08-27
Dalton Transactions
Abstract:A novel method, reduction followed by oxidation procedure, has been developed to fabricate the efficient electrodes derivated from metal-organic frameworks (MOFs), which were synthesized using terephthalic acid (TP) or 1,3,5-benzenetricarboxylic acid (BTC) as organic ligands. The copper-based composites, namely Cu/CuxO@C (x = 1 and 2), were obtained through two steps: first calcining the precursors at high temperature under nitrogen atmosphere, and then calcining in air to increase the porous active sites. For more convenient description, the calcined materials are denoted as 800-TP, 900-TP, 800-BTC and 900-BTC, respectively, according to the calcination temperature and the organic ligands simultaneously. Their electrochemical performances in supercapacitors (SCs) suggest that a higher calcination temperature endows the as-resulted materials with a larger specific surface area, higher carbon content, higher electrical conductivity, and better ion transport ability. For example, the 900-BTC electrode delivers a specific capacity of 400 C g-1 at a current density of 3 A g-1 under the three-electrode configuration. Even under the double-electrode system, the corresponding 900-BTC//AC device (AC represents activated carbon) also achieves superior electrochemical performance with an energy density of 24.02 Wh kg-1 at a power density of 825 W kg-1 and the specific capacitance retention for the device maintaining at 91.7% after 3000 unceasing loops, indicating its potential practical application.
chemistry, inorganic & nuclear