Abstract:A number of difficulties on the zinc surface, including dendrites, passivation, shape change, and corrosion, result in insufficient electrochemical performance. Additives having an S O anion group incorporated into organic/inorganic atoms offer varied charge distributions of molecules that may be effective in resolving problems. Four additives containing the SO anion group, such as 4-Morpholinepropanesulfonic acid (MOPS, organic) and Na 2 S 2 O 3 , Na 2 SO 3 , and Na 2 SO 4 (inorganic), reveal that 0.33 % ( v /v) 1 M Na 2 SO 4 /6 M KOH is the most effective electrolyte due to its good Zn-deposition/dissolution. The maximal specific capacity of 818 mAhg −1 at 50 mAcm −2 (material utilization of 99.8 % based on the value of 820 mAhg −1 ) is compared to 806 mAhg −1 for the electrolyte-free additive. The galvanostatic charge-discharge cycles demonstrate excellent and stable performance without any fluctuations with the lower voltage gap (1.07 V) for Na 2 SO 4 /KOH at 50 mAcm −2 for >100 h, which is significantly lower than 6 M KOH at around 1.2 V. (1.4 V). DFT analyses demonstrate that Na 2 SO 4 with the minimum energy gap (higher intrinsic conduction) are effective additives. As an organic additive, MOPS/KOH demonstrates an exceptional discharge capacity, but weak Zn-deposition/dissolution was seen due to the greatest energy gap, which resulted in less charge transfer interaction within the molecule.

The influence of S O anion groups of organic/inorganic additives in rechargeability of zinc-air batteries