Hydroxyapatite Formation in a Single-Stage Anammox-Based Batch Treatment System: Reactor Performance, Phosphorus Recovery, and Microbial Community
Albert Magrí,Emma Company,Frederic Gich,Jesús Colprim,Albert Magrí,Jesús Colprim
DOI: https://doi.org/10.1021/acssuschemeng.0c08036
2021-02-09
Abstract:Simultaneous ammonium–nitrogen (NH<sub>4</sub><sup>+</sup>–N) removal and orthophosphate–phosphorus (PO<sub>4</sub>–P) biomineralization was studied in two granular sludge sequencing batch reactors treating urban sidestream centrate through the one-stage partial nitritation–anaerobic ammonium oxidation (anammox) process. By adding an external source of calcium, concomitant conversion rates of up to 0.32 g NH<sub>4</sub><sup>+</sup>–N/(L·days) and 12 mg PO<sub>4</sub>–P/(L·days) were measured while reaching water-phase removal efficiencies of ca. 80% of the NH<sub>4</sub><sup>+</sup>–N and 70% of the PO<sub>4</sub>–P loaded. The mineral cores formed inside the granules were mostly composed of hydroxyapatite (HAP), which is a recoverable phosphate salt. Yet, the high mineralization of the sludge and its excessive purge from the bioreactor limited the microbial activity in the long term. In this sense, the densest granules, accumulated at the bottom of the bioreactor, were the most susceptible to being harvested because they were the richest in HAP, but at the same time, they contained the highest percentages of anammox bacteria.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c08036?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c08036</a>.Experimental setup (Figure S1); chemical analysis, biological tests, and calculations (Table S1, centrate characteristics; Figures S2, microscope observations; Figure S3, XRD pattern); and microbial community analysis (Table S2, α-diversity indexes; Figure S4, rarefraction curves; Figure S5, NMDS plots; Figure S6, relative abundances for AOB and AnAOB together with NCR) (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c08036/suppl_file/sc0c08036_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology