Abstract:The Yb(3+) and Er(3+) codoped orthorhombic LuF3 rectangular nanocrystals (NCs) with the size of about 10nm were synthesized by a facile and effective solvothermal process. X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), upconversion (UC) luminescence spectra and decay curves were used to characterize the resulting samples. Compared with YF3 and α-NaYF4 NCs, owning the similar size and the same doping levels of Yb(3+) ions and Er(3+) ions as LuF3 NCs, the green UC emission of LuF3 NCs is 18.7 times and 5.1 times stronger than that of YF3 and α-NaYF4 NCs respectively; the red UC emission of LuF3 NCs is 13.2 times and 0.6 times stronger than that of YF3 and α-NaYF4 NCs respectively. Under 980 nm wavelength excitation, the decay curves of both (4)S3/2→(4)I15/2 transition and (4)F9/2→(4)I15/2 transition exhibit a single exponential function, resulting from the fast energy migrations among Yb(3+) ions caused by the high concentration of Yb(3+) ions (20 mol%). Meanwhile, at relatively low power density, the slopes of the linear plots between log(I) and log(P) for green UC and red UC are 1.7 and 1.9 respectively, which are less than 2 due to the quenching of the thermal effect, indicating a two-photon process for them. At high power density, the slopes are decreased caused by the saturation effect. In addition, we proved the existence of the thermal effect by the pump power dependence of the intensity ratio of (2)H11/2→(4)I15/2 transition to (4)S3/2→(4)I15/2 transition.

Solvothermal synthesis and upconversion properties of YF3:Ln (Ln = Yb/Er,Yb/Tm,Yb/Ho) nanoparticles

Synthesis and Luminescence Properties of Lanthanide (Iii)-Doped YF3 Nanoparticles

Synthesis of LaF3: Yb3+,Ln3+nanoparticles with Improved Upconversion Luminescence

Controllable hydrothermal synthesis of NaYbF4 and YbF3 with diverse morphologies and emission enhancement in β-NaYbF4: Er3+ upconversion micro-crystals via solvents codoping and Na+ dosage

Controllable synthesis and up-conversion properties of tetragonal BaYF5:Yb/Ln (Ln=Er, Tm, and Ho) nanocrystals.

Molten salt synthesis of tetragonal LiYF4:Yb3+/ Ln3+ (Ln = Er, Tm, Ho) microcrystals with multicolor upconversion luminescence

Solvothermal Synthesis and Upconversion Properties of about 10 Nm Orthorhombic Luf3: Yb3+, Er3+ Rectangular Nanocrystals

Lanthanide-doped LiYF4 Nanoparticles: Synthesis and Multicolor Upconversion Tuning

Controlled synthesis and upconversion luminescence properties of LiYF4:Yb0.2Er0.02 nanoparticles

Controllable Synthesis and Upconversion Luminescenceof NaYF4:Yb3+, Er3+ Nanocrystals

Solvothermal synthesis and upconversion properties of about 10 nm orthorhombic LuF₃: Yb³⁺, Er³⁺ rectangular nanocrystals

Solvothermal Synthesis and Tunable Luminescence of Tb3+, Eu3+ Codoped Yf3 Nano- and Micro-Crystals with Uniform Morphologies

Tuning upconversion luminescence of LiYF4:Yb3+,Er3+/Tm3+/Ho3+ microcrystals synthesized through a molten salt process

Preparation of upconversion luminescent NaYF4 co-doped with Yb3+/Er3+ via hydrothermal synthesis

Hydrothermal synthesis and luminescence properties of YF3:Ln (Ln=Sm, Dy, Tb and Pr) nano-/microcrystals

Solvothermal synthesis and upconversion properties in Yb3+/Ln3+ (Ln3+=Er3+/ Ho3+/ Tm3+) codoped In2O3 nanoparticles with fine stability

pH value manipulated phase transition, microstructure evolution and tunable upconversion luminescence in Yb(3+)-Er(3+) codoped LiYF4/YF3 nanoparticles

Enhanced Blue and Green Upconversion in Hydrothermally Synthesized Hexagonal NaY1−xYbxF4:Ln3+ (ln3+ = Er3+ or Tm3+)

Synthesis and Intense Ultraviolet to Visible Upconversion Luminescence of YF3:Ho3+ Nanoparticles

The synthesis, crystal structure and multicolour up-conversion fluorescence of Yb3+/Ln3+ (Ln = Ho, Er, Tm) codoped orthorhombic lutetium oxyfluorides

Down/Up Conversion in Ln(3+)-Doped Yf3 Nanocrystals