Abstract:A series of thermoresponsive core-shell microgels were synthesized using SiO2 as core and hybrid gel (hyaluronate/poly(N-isopropylacrylamide) (HA/PNIPAm)) as shell. SiO2 particles were modified by KH550 to get -NH2 groups, which could be protonized in acid condition. So that they could be covered by HA chains through electrostatic force. Then, HA was grafted using glycidyl methacrylate (GMA) to obtain C=C groups for the next synthesis of 1.1261/PNIPAm hybrid gel. The modification degree of C=C was determined through H-1 nuclear magnetic resonance spectroscopy (H-1 NMR). Fourier-transform infrared spectra (FT-IR) were used to monitor each synthesis step. Transmission electron microscopy (TEM) images showed that SiO2-HA/PNIPAm microgels were almost monodispersed and possessed perfect core-shell structures. Thermoresponsive behaviors of microgels were investigated using micro-differential scanning calorimetry (Micro-DSC), which showed that the lower critical solution temperature (LCST) values were almost the same, around 34 +/- 0.1 degrees C, regardless of the synthetic parameters. The thixotropy of SiO2-HA/PNIPAm microgels was studied using rheometer. It turned out that the microgels possessed negative thixotropy. Moreover, when the temperature was higher than LCST, the thixotropy was better than that of lower temperature. The swelling behaviors of SiO2-HA/PNIPAm microgels were evaluated by combining experiment methods and theoretical calculation. Dynamic light scattering (DLS) was used to analyze the swelling behavior of microgels with the increase of temperature. The DLS results showed that microgels possessed good thermoresponsive behavior with a LCST at about 34 which was in accordance with that determined by Micro-DSC. The hydrodynamic diameter (d) was found to be dependent on the size of core, the Ad, of HA and the amount of PNIPAm. Theoretical calculation was carried out using a lattice molecular thermodynamic model based on our previous works, it showed that the calculated results were in good agreement with the experimental data. The results indicated that the model could predict the swelling behavior of thermoresponsive core-shell structured microgel using fewer model parameters. This work will provide fundamental reference for further research.

One-step microfluidic synthesis of Janus microhydrogels with anisotropic thermo-responsive behavior and organophilic/hydrophilic loading capability

Synthesis of Poly(N-isopropylacrylamide) Janus Microhydrogels for Anisotropic Thermo-responsiveness and Organophilic/Hydrophilic Loading Capability

Functional stimuli responsive hydrogel devices by self-folding

Thermo-sensitive ionic microgels via post quaternization cross-linking: fabrication, property, and potential application

Thermosensitive ionic microgels via surfactant-free emulsion copolymerization and in situ quaternization cross-linking.

One-step synthesis of Janus hydrogel via heterogeneous distribution of sodium α-linoleate driven by surfactant self-aggregation

Multiresponsive Microgels with Phase-Separated Nanodomains and Self-Regulating Properties Via Incorporation of Anthraquinone Moieties.

Poly( N-isopropylacrylamide- Co-1-vinyl-3-alkylimidazolium Bromide) Microgels with Internal Nanophase-Separated Structures.

Poly(N-isopropylacrylamide)-based Ionic Hydrogels : Synthesis, Swelling Properties, Interfacial Adsorption and Release of Dyes

Friction-directed self-assembly of Janus lithographic microgels into anisotropic 2D structures.

One-pot Synthesis of Janus Nanosheets on Strengthening and Toughening Nanocomposite Double Network Hydrogels

Synthesis of macroporous thermosensitive hydrogels: a novel method of controlling pore size.

Temperature-Sensitive Anti-Inflammatory Organohydrogels Containing Janus Particle Stabilized Phase-Change Microinclusions

Preparation of Janus Droplets and Hydrogels with Controllable Morphologies by an Aqueous Two-Phase System on the Superamphiphobic Surface

Preparation and properties of thermo-sensitive organic/inorganic hybrid microgels

Microfluidics assisted generation of innovative polysaccharide hydrogel microparticles

Synthesis and Properties of Organic-Inorganic Hybrid P(Nipam-Co-Am-Co-Tmspma) Microgels

Multicompartmental Janus microbeads from branched polymers by single-emulsion droplet microfluidics

Synthesis and Swelling Behavior of Sio2-Ha/Pnipam Core-Shell Structured Thermoresponsive Microgels

Synthesis and characterization of stimuli‐sensitive micro‐ and nanohydrogels based on photocrosslinkable poly(dimethylaminoethyl methacrylate)

Microfluidic generation of monodispersed Janus alginate hydrogel microparticles using water-in-oil emulsion reactant.