Abstract:In this work, the formation of laser-induced periodic surface structures (LIPSS) on the surfaces of thin films of poly(ethylene terephthalate) (PET) and PET reinforced with expanded graphite (EG) was studied. Laser irradiation was carried out by ultraviolet (265 nm) and near-infrared (795 nm) femtosecond laser pulses, and LIPSS were formed in both materials. In all cases, LIPSS had a period close to the irradiation wavelength and were formed parallel to the polarization of the laser beam, although, in the case of UV irradiation, differences in the formation range were observed due to the different thermal properties of the neat polymer in comparison to the composite. To monitor the modification of the physicochemical properties of the surfaces after irradiation as a function of the laser wavelength and of the presence of the filler, different techniques were used. Contact angle measurements were carried out using different reference liquids to measure the wettability and the solid surface free energies. The initially hydrophilic surfaces became more hydrophilic after ultraviolet irradiation, while they evolved to become hydrophobic under near-infrared laser irradiation. The values of the surface free energy components showed changes after nanostructuring, mainly in the polar component. Additionally, for UV-irradiated surfaces, adhesion, determined by the colloidal probe technique, increased, while, for NIR irradiation, adhesion decreased. Finally, nanomechanical properties were measured by the PeakForce Quantitative Nanomechanical Mapping method, obtaining maps of elastic modulus, adhesion, and deformation. The results showed an increase in the elastic modulus in the PET/EG, confirming the reinforcing action of the EG in the polymer matrix. Additionally, an increase in the elastic modulus was observed after LIPSS formation.

Femtosecond laser carbonization of polystyrene

Turning a polystyrene microsphere into a multimode light source by laser irradiation

Degradation of Polystyrene on Silver Substrates during Surface-Enhanced Raman Scattering

Femtosecond laser-induced surface wettability modification of polystyrene surface

Femtosecond laser micro-structuring of amorphous polyether(ether)ketone at 775 nm and 387 nm

Femtosecond Er-Doped All-Fiber Laser with High-Density Well-Aligned Carbon-Nanotube-Based Thin-Film Saturable Absorber

Composition conversion and parameters influence of nanosecond ultraviolet laser cutting polystyrene film

Nanopatterning of the dielectric surface by a pair of femtosecond laser pulses of different colors through a monolayer of microspheres

Laser-assisted surface processing for functionalization of polymers on micro- and nano-scale

Carbonization of a Molybdenum Substrate Surface and Nanoparticles by a One-Step Method of Femtosecond Laser Ablation in a Hexane Solution

Large-area fabrication of low- and high-spatial-frequency laser-induced periodic surface structures on carbon fibers

Formation of Deep-Subwavelength Structures on Organic Materials by Femtosecond Laser Ablation

Physicochemical Modifications on Thin Films of Poly(Ethylene Terephthalate) and Its Nanocomposite with Expanded Graphite Nanostructured by Ultraviolet and Infrared Femtosecond Laser Irradiation

Optical Microstructures Fabricated by Femtosecond Laser Two-Photon Polymerization

[Fabrication and Surface-Enhanced Raman Scattering Research on Polystyrene Nanospheres Arrays].

Structural Transformations of a Carbon Nanomaterial under High-Energy Laser Irradiation

Polymer surface reactivity enhancement by ultraviolet ArF laser irradiation: An x‐ray photoelectron spectroscopy study of polytetrafluoroethylene and polyethyleneterepthalate ultraviolet treated surfaces

Functionalization of Multiwalled Carbon Nanotubes with Polystyrene under Atom Transfer Radical Polymerization Conditions

Surface modification of multiwalled carbon nanotubes via nitroxide-mediated radical polymerization

Femtosecond Laser Ablated Polymer SERS Fiber Probe with Photoreduced Deposition of Silver Nanoparticles

Laser irradiation of photothermal precursors ‐ a novel approach to produce carbon materials for supercapacitors