A facile route to synthesize cubic gauche polymeric nitrogen

Runteng Chen,Jun Zhang,Zelong Wang,Ke Lu,Yi Peng,Jianfa Zhao,Xiaodong Liu,Shaomin Feng,Ruibin Liu,Chuan Xiao,Changqing Jin

DOI: https://doi.org/10.1016/j.scib.2024.11.004

2024-11-16

Abstract:In this work, the long-sought cg-N with N-N single bond has been synthesized for the first time by a thermal-driven-only chemical route at ambient conditions. The successful synthesis of cg-N was achieved by first creating a solution of azides, which was then pretreated under vacuum conditions. Following the pretreatment, the resultant concentrated azide was heated at temperatures ranging from 260°C to 330°C for a reaction time of 3 hours, ultimately leading to the formation of cg-N. The emergent intense Raman peak characterized of cg-N provides solid evidence that the double bonded nitrogen-nitrogen transforms into a single bond form, which agrees well with cg-N structure. To date, this is the only work achieving the quantity of cg-N synthesized at ambient conditions by a facile route that can be further developed for the scalable synthesis and applications of polymerized nitrogen-based materials as high energy density materials.

Materials Science,Superconductivity,Chemical Physics

What problem does this paper attempt to address?

This paper aims to solve the problem of how to simply synthesize cubic gauche nitrogen (cg - N) at room temperature and normal pressure. cg - N is a polymeric nitrogen material with a single - bond structure. Due to its significant energy density advantage, it is considered as one of the important candidates for high - energy materials. Previously, the synthesis of cg - N usually required extremely high pressure and temperature conditions, which limited the possibility of its practical application. This article reports a new method for successfully synthesizing cg - N through a thermally - driven chemical pathway at room temperature and normal pressure, providing the possibility for future large - scale production and application of polymeric nitrogen - based high - energy materials. The synthesis process is described in detail in the paper, including using an azide solution as a precursor. After vacuum pretreatment, it is heated in the temperature range of 260 °C to 330 °C for 3 hours, and finally cg - N is formed. Through Raman spectroscopy analysis, the successful synthesis of cg - N is confirmed. In particular, the characteristic peak of cg - N appears at 635 cm⁻¹, and this finding is consistent with theoretical predictions. In addition, thermogravimetric - differential scanning calorimetry (TG - DSC) analysis further verifies the thermal stability of cg - N, showing its decomposition characteristics at 477 °C. These results not only prove the effectiveness of the new synthesis method but also provide important experimental bases for subsequent research.

A facile route to synthesize cubic gauche polymeric nitrogen

A simple route to synthesize cubic gauche polymeric nitrogen

Charge transfer induced cubic gauche nitrogen from azides

One-step Synthesis of Cubic Gauche Polymeric Nitrogen with High Yield Just by Heating

Free-standing cubic gauche nitrogen stable at 760 K under ambient pressure

Polymerization of Nitrogen in Cesium Azide under Modest Pressure

Route to stabilize cubic gauche polynitrogen to ambient conditions via surface-saturation by hydrogen

All-Nitrogen Energetic Material Cubic Gauche Polynitrogen: Plasma Synthesis and Thermal Performance

Synthesis and characterization of nitrogen-rich graphitic carbon nitride

Synthesis of nitrogen-doped carbon nanostructures by the reactions of small molecule carbon halides with sodium azide.

A Facile Route to Metal Nitride Clusterfullerenes by Using Guanidinium Salts: A Selective Organic Solid As the Nitrogen Source

Facile Syntheses of Spherical and Nubbly Nitrogen-Containing Carbon Materials from Imidazo[1,2-A]pyridin-2-one and Furfural

All-Single Bonds Fused N18 Macro-Rings and N8 Cagelike Building Blocks Stabilized in Lanthanum Supernitrides

Nitrogen-rich GaN5 and GaN6 As High Energy Density Materials with Modest Synthesis Condition

Aroylacetylene-Based Amino-Yne Click Polymerization Toward Nitrogen-Containing Polymers

Synthesis and characterization of polyether structure carbon nitride

Achieving high-energy-density crown-like polymeric nitrogen cr-N via chelate CeN8

High-pressure and high-temperature induced polymerization of confined nitrogen

Regioisomeric functionalization of azo-bridged nitropyrazoles: Pushing the density limit of catenated nitrogen systems

Low-Temperature Synthesis of Solution Processable Carbon Nitride Polymers