Increased resistance to photooxidation in Dion-Jacobson lead halide perovskites -- implication for perovskite device stability

Zhilin Ren,Juraj Ovčar,Tik Lun Leung,Yanling He,Yin Li,Dongyang Li,Xinshun Qin,Hongbo Mo,Zhengtian Yuan,Jueming Bing,Martin P. Bucknall,Luca Grisanti,Muhammad Umair Ali,Peng Bai,Tao Zhu,Ali Ashger Syed,Jingyang Lin,Jingbo Wang,Abdul-Khaleed,Wenting Sun,Gangyue Li,Gang Li,Alan Man Ching Ng,Anita W. Y. Ho-Baillie,Ivor Lončarić,Jasminka Popović,Aleksandra B. Djurišić

2024-09-19

Abstract:2D metal halide perovskites have enabled significant stability improvements in perovskite devices, particularly in resistance to moisture. However, some 2D perovskites are even more susceptible to photooxidation compared to 3D perovskites. This is particularly true for more commonly investigated Ruddlesden-Popper (RP) perovskites that exhibit increased susceptibility to photoinduced degradation compared to Dion-Jacobson (DJ) perovskites. Comparisons between different RP and DJ perovskites reveal that this phenomenon cannot be explained by commonly proposed differences in superoxide ion generation, interlayer distance and lattice structural rigidity differences. Instead, the resistance to photooxidation of DJ perovskites can be attributed to decreased likelihood of double deprotonation events (compared to single deprotonation events in RP perovskites) required for the loss of organic cations and the perovskite decomposition. Consequently, DJ perovskites are less susceptible to oxidative degradation (both photo- and electrochemically induced), which leads to improved operational stability of solar cells based on these materials.

Materials Science,Applied Physics

What problem does this paper attempt to address?

The problem this paper attempts to address is: improving the stability of perovskite solar cells under illumination conditions, particularly photo-oxidative stability. Specifically, the researchers focused on the degradation mechanisms of two types of two-dimensional (2D) metal halide perovskite materials—Ruddlesden-Popper (RP) and Dion-Jacobson (DJ) perovskites—under illumination conditions and explored why DJ perovskites exhibit better photo-oxidative stability than RP perovskites.

### Main Issues:
1. **Photo-oxidative Stability**: 3D metal halide perovskites tend to degrade under conditions of light, oxygen, and humidity, leading to a decline in device performance. Although 2D perovskites have somewhat improved these stability issues, their photo-oxidative stability under illumination still requires further research.
2. **Degradation Mechanisms**: Researchers aim to understand the specific degradation mechanisms of RP and DJ perovskites under illumination, especially why DJ perovskites show higher photo-oxidative stability.
3. **Generality of Stability**: To verify whether the stability improvement of DJ perovskites is consistent and generalizable across different 3D perovskite combinations.

### Solutions:
- **Experimental Methods**: Using various techniques such as absorption spectroscopy, FTIR spectroscopy, electron paramagnetic resonance (EPR) spectroscopy, and electrochemical testing to study the photo-oxidative behavior of RP and DJ perovskites under different environmental conditions.
- **Theoretical Calculations**: Conducting density functional theory (DFT) calculations to explore the energy changes and structural stability of different types of perovskite materials under illumination.
- **Device Testing**: Fabricating solar cells with different combinations of 3D and 2D perovskites and testing their performance and stability under illumination.

### Main Findings:
- **Differences in Photo-oxidative Stability**: DJ perovskites exhibit significantly better stability under illumination compared to RP perovskites. This is mainly attributed to the lower occurrence of double deprotonation events in DJ perovskites, which reduces the loss of organic cations and the decomposition of the perovskite.
- **Degradation Mechanisms**: RP perovskites are prone to single deprotonation events under illumination, leading to the loss of organic cations and degradation of the perovskite layers. In contrast, DJ perovskites require double deprotonation events to form vacancies, a process that is more difficult, thus resulting in higher stability.
- **Generality Verification**: Devices using 2D DJ perovskites as capping layers in different 3D perovskite combinations show better stability, confirming the generality of DJ perovskites in improving photo-oxidative stability.

Through these studies, the paper provides important theoretical and experimental evidence for developing more stable perovskite solar cells.