Durably Ductile, Transparent Polystyrene Based on Extensional Stress-Induced Rejuvenation Stabilized by Styrene–Butadiene Block Copolymer Nanofibrils
Ying Zeng,Qian-Cheng Yang,Ying-Te Xu,Guo-Qi Ma,Hua-Dong Huang,Jun Lei,Gan-Ji Zhong,Zhong-Ming Li
DOI: https://doi.org/10.1021/acsmacrolett.0c00733
IF: 5.8
2020-12-18
ACS Macro Letters
Abstract:The glassy polymer of polystyrene (PS) enjoys a good reputation as a promising optical material; however, the inherent brittleness hinders its further applications. Conventional toughening methods are realized based on the premise of a sacrifice in transparency and stiffness. In this work, we found an unprecedented strategy to address these obstacles by combining extensional stress-induced ductility and suppressing physical aging. PS-based film with a high stiffness, long-term ductility, and excellent transparency is achieved by introducing a styrene–butadiene block copolymer into the PS matrix and subsequently annealing stretched. A nanofibrillar structure of the polybutadiene (PB) phase is formulated surrounded by a PS matrix, and thus, the elongation at break enhances from 3.1% up to 86.8%, accompanying the yield strength enhanced from 25.5 to 62.2 MPa. More significantly, compared with neat PS, these films survive from physical aging and persistent ductility over time. The morphology deformation induced by stress makes an obvious contribution to the improvement of transparency. Investigating the dynamics of chain segments indicates that the incorporation of the copolymer can restrict rearrangement and local relaxation to the PS chain. This work could pave a potential route toward high-performance PS and might be transferable to other glassy polymers with a fragile character.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsmacrolett.0c00733?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsmacrolett.0c00733</a>.Materials, sample preparation, and protocol; the calculation procedure of the average length of PB nanofibrils (<i>L</i><sub>f</sub>) by SAXS profiles; 2D-SAXS pattern and <i>L</i><sub>f</sub> of the films; the TEM images of 30 wt %, 50 wt % blend, and neat KR01; the mechanical properties of the neat KR01 unstretched films; comparison of mechanical and optical properties between toughening methods from the recent reports and our work; the typical stress–strain curves of the neat PS and 15 wt % blend films after 1 and 106 days of storage at room temperature, respectively; the mechanical properties of neat PS films and 15 wt % blend films after 407 days of storage; detailed information on optical properties in neat KR01 films; the orientation factor (<i>f</i>) of samples with diverse KR01 content and draw ratios; the TMDSC profiles of samples with diverse draw ratios; the calculation procedure of mass fraction of mobile amorphous fraction (MAF) and the rigid amorphous fraction (RAF); the DMA curves of specimens with various draw ratios (<a class="ext-link" href="/doi/suppl/10.1021/acsmacrolett.0c00733/suppl_file/mz0c00733_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
polymer science