Properties of promising cartilage implants based on cellulose-polyacrylamide composite hydrogels: results of in vivo tests carried out over a period of 90-120 days

Alexander Buyanov,Iosif Gofman,Svetlana Bozhkova,Natalia Saprykina,Georgii Netylko,Evgenii Panarin

2024-08-04

Abstract:High-strength composite hydrogels cellulose-polyacrylamide were synthesized by free-radical polymerization of acrylamide conducted inside the previously formed physical network of regenerated plant cellulose. Partial hydrolysis of the amide groups of these hydrogels yielded their ionic forms with a degree of hydrolysis of 0.1 and 0.25. The cylindrical hydrogel samples of three compositions were implanted in the preformed osteochondral defects of the rabbit's femoral knee joints. No signs of migration or disintegration of the tested implants were revealed in the course of in vivo tests as long as 90 and 120 days after the implantation. The mechanical behavior of both the virgin hydrogels-implants and the implants extracted from the joints after in vivo experiments was studied in detail. The morphology and chemical composition of the extracted implants were studied by SEM combined with the EDX method. The results obtained were shown that the mechanical characteristics of hydrogel implants remained practically unchanged after in vivo tests. The extracted implants, as well as the initial hydrogels, endured cyclic compression loading at the amplitude up to 50 %. Compression stresses up to 3-10 MPa were recorded in these tests, which is close to the data obtained by several authors for natural articular cartilages in the same conditions of loading. The principal differences in the chemical composition and morphology of the implant area adjacent to the subchondral bone for non-ionic and ionic types of implants have been revealed. If for non-ionic types of implants in this area intensive mineralization with formation of calcium phosphates inside the polymeric hydrogel network is observed, the border area of ionic implants practically does not undergo mineralization.

Chemical Physics

What problem does this paper attempt to address?

The problem this paper attempts to address is the development of a high-performance artificial cartilage implant based on cellulose/polyacrylamide composite hydrogels to replace damaged joint cartilage tissue. Specifically, the researchers synthesized high mechanical strength composite hydrogels through a radical polymerization method and conducted detailed studies on their biocompatibility and mechanical properties in animal models.

### Main Research Questions:
1. **Mechanical Performance**: Investigate the mechanical performance of the synthesized composite hydrogels under compressive load, particularly whether their stress values under 30-50% compressive deformation can meet the physiological requirements of joint cartilage (3-10 MPa).
2. **Biocompatibility**: Evaluate the biocompatibility of these composite hydrogels when implanted in animals, including whether there is any migration, degradation, or inflammatory response.
3. **Mineralization Process**: Study the mineralization process of the hydrogels in the area of contact with bone tissue in vivo, especially the effect of introducing ionic carboxylate groups on mineralization.
4. **Long-term Stability**: Assess the mechanical performance and morphological changes of these hydrogels after 90-120 days in vivo to determine their long-term stability as artificial cartilage implants.

### Research Background:
- **Properties of Hydrogels**: Hydrogels are elastic networks composed of hydrophilic polymers. Due to their high water content and good biocompatibility, they are widely used in biomedical fields such as wound dressings, contact lenses, and drug delivery systems.
- **Cartilage Replacement Materials**: Currently, hydrogels are also being studied for replacing damaged joint cartilage tissue. However, existing hydrogel materials still have deficiencies in mechanical performance and cannot fully mimic the mechanical properties of natural joint cartilage.
- **Composite Hydrogels**: By incorporating cellulose as a reinforcing component into other polymers, the mechanical performance of hydrogels can be significantly improved. The composite hydrogels in this study were prepared by a radical polymerization method, with cellulose serving as a rigid framework and polyacrylamide as the elastic component.

### Experimental Design:
- **Sample Preparation**: Three different compositions of composite hydrogel samples were prepared and implanted into cartilage defects in the knee joints of rabbits.
- **Mechanical Testing**: Single compression and cyclic compression tests were conducted on the initial hydrogel samples and the hydrogel implants retrieved from animals to evaluate their mechanical performance.
- **Morphological and Chemical Analysis**: Scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDX) were used to analyze the morphology and chemical composition of the retrieved implants.
- **In Vivo Experiments**: The biocompatibility and mineralization process of the implants were observed over 90-120 days.

### Research Objectives:
- **Verify Mechanical Performance**: Confirm whether the composite hydrogels can maintain their mechanical performance after long-term use in vivo, particularly the stress values under 30-50% compressive deformation.
- **Evaluate Biocompatibility**: Ensure that the implants do not cause inflammation or other adverse reactions and can remain stable in vivo.
- **Regulate Mineralization Process**: Control the mineralization process of the hydrogels in the area of contact with bone tissue by introducing ionic carboxylate groups to avoid the impact of mineralization on cartilage function.

Through these studies, the paper aims to develop a high-performance artificial cartilage implant that can effectively replace damaged joint cartilage tissue and has good biocompatibility and mechanical performance.