Thermal conductivity in modified oxide glasses is governed by modal phase changes

Philip Rasmussen,Søren Strandskov Sørensen

2024-08-01

Abstract:The thermal conductivity of glasses is well-known to be significantly harder to theoretically describe compared to crystalline materials. Because of this fact, the fundamental understanding of thermal conductivity in glasses remain extremely poor when moving beyond the case of simple glasses, e.g., glassy SiO$_2$, and into so-called 'modified' oxide glasses, that is, glasses where other oxides (e.g. alkali oxides) have been added to break up the network and alter e.g. elastic and thermal properties. This lack of knowledge is apparent despite how modified glasses comprise the far majority of known glasses. In the present work we study an archetypical series of sodium silicate ($x\text{Na}_2\text{O}\text{-}(100\text{-}x)\text{SiO}_2$) glasses. Analyses of modal contributions reveal how increasing Na$_2$O content induces increasing vibrational localization with a change of vibrations to be less ordered, and a related general decrease in modal contributions to thermal conductivity. We find the vibrational phases (acoustic vs. optical) of sodium vibrations to be relatively disordered compared to the network-forming silicon and oxygen species, explaining how increasing Na$_2$O content decreases thermal conductivity. Our work sheds new light on the fundamentals of glassy heat transfer as well as the interplay between thermal conduction and modal characteristics in glasses.

Disordered Systems and Neural Networks

What problem does this paper attempt to address?

The paper is primarily dedicated to addressing the understanding of thermal conductivity mechanisms in modified oxide glasses. Specifically, the study focuses on the sodium silicate glass system (xNa₂O-(100-x)SiO₂), where x ranges from 20 to 35 mol%. The core issue of the research is to understand and explain the changes in thermal conductivity as the Na₂O content increases.

The main contributions of the paper include:

1. **Validation of Structural and Mechanical Properties**: By comparing with experimental data, it was verified that the Teter potential function can well describe the structure and mechanical properties of the simulated glass. This includes good matching of the structure factor and consistency of elastic moduli (such as Young's modulus, bulk modulus, and shear modulus) with experimental values.
2. **Vibrational Characteristics Analysis**: Through detailed analysis of the vibrational density of states (VDOS), it was found that as the Na₂O content increases, the vibrations in the low-frequency region (0-10 THz) are mainly contributed by sodium ions, while changes in the 10-25 THz range are primarily caused by oxygen atoms.
3. **Mode Participation Ratio Study**: By calculating the mode participation ratio (PR), researchers found that the vibrational modes in the mid-frequency region (10-20 THz) have higher PR values, indicating that the atomic vibrations in these modes contribute more uniformly to the overall vibration. As the Na₂O content increases, the PR in the mid-frequency region decreases and shifts to the low-frequency region, which is related to the increased contribution of Na⁺ ions to the vibrational characteristics.
4. **Thermal Conductivity Prediction**: Using the Quasi Harmonic Green-Kubo method combined with the Teter potential function, the thermal conductivity of sodium silicate glass with different Na₂O contents was successfully predicted and compared with experimental results. The results show that as the Na₂O content increases, the thermal conductivity gradually decreases, which is related to the enhanced vibrational localization caused by sodium ions.

In summary, this study provides new insights into the thermal transport mechanisms in modified oxide glasses and contributes to the future development of new materials with specific thermal conductivity requirements.