Abstract:Iron chalcogenides superconductors, such as Fe(Te,Se) have recently garnered significant attention due to their simple crystal structure with a relatively easy synthesis process, high-temperature superconductivity, intrinsic topological band structure, and an unconventional pairing of superconductivity with ferromagnetism. Here, we report the complex in-plane refractive index measurement of nanometer-thin Fe(Te,Se) flake exfoliated from a single crystal FeTe$_{\text{0.6}}$Se$_{\text{0.4}}$ for photon wavelengths from 450 to 1100 nm over a temperature range from 4 K to 295 K. The results were obtained by employing a two-Drude model for the dielectric function of Fe(Te,Se), a multiband superconductor, and fitting the absolute optical reflection spectra using the transfer matrix method. A high extinction coefficient in the visible to near-infrared range makes nanometer-thin Fe(Te,Se) flakes a promising material for photodetection applications.
What problem does this paper attempt to address?
This paper aims to solve the problem of measuring the temperature - dependent optical constants of the iron - based superconductor Fe(Te,Se) in the visible and near - infrared bands. Specifically, the researchers experimentally measured the complex - plane refractive index (\(\tilde{n} = n + ik\)) of nano - thickness Fe(Te,Se) flakes in the temperature range from 4 K to 295 K and the wavelength range from 450 nm to 1100 nm. These measurement results are of great significance for understanding the optical properties of Fe(Te,Se) and its potential applications in photonics and quantum photonics.
### Main research contents:
1. **Material preparation and characterization**:
- The researchers exfoliated nano - thickness Fe(Te,Se) flakes from single - crystal FeTe\(_{0.6}\)Se\(_{0.4}\) and transferred them onto a SiO\(_2\)/Si substrate.
- The thickness of the flakes was determined to be 7.6 nm, corresponding to about 12 layers, using an atomic force microscope (AFM).
2. **Optical reflectance measurement**:
- Reflectance measurements were carried out using a broadband light source and a high - numerical - aperture objective lens (NA = 0.8). The reflected light was collected and the data were recorded using a spectrometer.
- The absolute reflectance at different temperatures was measured, and the thickness - dependent reflectance spectra were fitted using the transfer matrix method.
3. **Complex - plane refractive index calculation**:
- The two - Drude model was used to describe the complex dielectric function \(\tilde{\epsilon}\) of Fe(Te,Se), and the experimental data were fitted using the transfer matrix method.
- The complex dielectric function in the model is expressed as:
\[
\tilde{\epsilon}(\omega) = \epsilon_\infty - \frac{\omega_p^2}{\omega^2 + i\omega\gamma} + \sum_j \frac{\Omega_j^2}{\omega_j^2 - \omega^2 - i\omega\Gamma_j}
\]
where \(\epsilon_\infty\) is the real part in the high - frequency limit, \(\omega_p\) and \(\gamma\) are the plasma frequency and scattering rate respectively, and \(\Omega_j\), \(\omega_j\) and \(\Gamma_j\) are the intensity, position and width of the \(j\) - th bound excitation respectively.
4. **Result analysis**:
- At 4 K, the variation ranges of the refractive index \(n\) and the extinction coefficient \(k\) are 2.81 - 4.26 and 2.24 - 3.21 respectively.
- At 295 K, the variation ranges of the refractive index \(n\) and the extinction coefficient \(k\) are 2.79 - 4.38 and 2.14 - 3.04 respectively.
- With the increase of temperature, a blue - shift phenomenon of the low - energy oscillator position was observed. For example, at 10 K, the refractive index peak position blue - shifted from 493 nm at 4 K to 482 nm, and the extinction coefficient minimum position blue - shifted from 553 nm at 4 K to 542 nm.
### Conclusion:
This study provides detailed temperature - dependent optical constants of Fe(Te,Se) in the visible and near - infrared bands. These data are helpful for understanding its optical properties at different temperatures and provide an important reference for its applications in photonics and quantum photonics. In particular, Fe(Te,Se) exhibits a high extinction coefficient at room temperature, making it a candidate material for high - performance photodetectors.