Pseudosymmetry in Tetragonal Perovskite SrIrO$_3$ Synthesized under High Pressure

Haozhe Wang,Alberto de la Torre,Joseph T. Race,Qiaochu Wang,Jacob P. C. Ruff,Patrick M. Woodward,Kemp W. Plumb,David Walker,Weiwei Xie

2024-07-11

Abstract:In this study, we report a tetragonal perovskite structure of SrIrO$_3$ (P4/mmm, a = 3.9362(9) Å, c = 7.880(3) Å) synthesized at 6 GPa and 1400 $°$C, employing the ambient pressure monoclinic SrIrO$_3$ with distorted 6H structure as a precursor. The crystal structure of tetragonal SrIrO3 was evaluated on the basis of single crystal and powder X-ray diffraction. A cubic indexing was observed attributed to overlooked superlattice reflections. Weak fractional peaks in the H and K dimensions suggest possible structure modulation by oxygen defects. Magnetization study reveals weak paramagnetic behavior down to 2 K, indicative of the interplay between spin-orbit coupling, electron correlations, and crystal electric field. Additionally, measurements of electrical resistivity display metallic behavior with an upturn at about 54 K, ascribed to weak electron localization and possible structural defects.

Materials Science

What problem does this paper attempt to address?

This paper mainly explores the synthesis of tetragonal perovskite structure SrIrO3 under high pressure. The research team successfully synthesized tetragonal SrIrO3 (P4/mmm space group, a = 3.9362(9) Å, c = 7.880(3) Å) by using the initial monoclinic structure SrIrO3 as a precursor under high temperature and high pressure conditions of 6 GPa and 1400 °C. Single crystal and powder X-ray diffraction analysis excluded the possibility of pseudocubic symmetry and discovered structural modulation possibly caused by oxygen defects in the H and K dimensions.

The paper also investigates the magnetic and electrical transport properties of the material. Magnetization measurements show weak paramagnetic behavior of tetragonal SrIrO3 at 2 K, indicating the interaction between spin-orbit coupling, electronic correlations, and crystal field. Electrical conductivity measurements reveal metallic characteristics, but a resistance increase occurs at around 54 K, possibly due to weak electron localization and structural defects.

In summary, the main contribution of the paper is the report of a novel high-pressure synthesized tetragonal SrIrO3, which exhibits different behaviors in terms of structure, magnetism, and electrical properties compared to conventional materials, especially under the influence of spin-orbit coupling. These findings are of great significance for understanding quantum physical phenomena in 5d transition metal compounds.