Bulk high-temperature superconductivity in the high-pressure tetragonal phase of bilayer La2PrNi2O7

Ningning Wang,Gang Wang,Xiaoling Shen,Jun Hou,Jun Luo,Xiaoping Ma,Huaixin Yang,Lifen Shi,Jie Dou,Jie Feng,Jie Yang,Yunqing Shi,Zhian Ren,Hanming Ma,Pengtao Yang,Ziyi Liu,Yue Liu,Hua Zhang,Xiaoli Dong,Yuxin Wang,Kun Jiang,Jiangping Hu,Stuart Calder,Jiaqiang Yan,Jianping Sun,Bosen Wang,Rui Zhou,Yoshiya Uwatoko,Jinguang Cheng

2024-07-08

Abstract:The Ruddlesden-Popper (R-P) bilayer nickelate, La3Ni2O7, was recently found to show signatures of high-temperature superconductivity (HTSC) at pressures above 14 GPa. Subsequent investigations achieved zero resistance in single- and poly-crystalline samples under hydrostatic pressure conditions. Yet, obvious diamagnetic signals, the other hallmark of superconductors, are still lacking owing to the filamentary nature with low superconducting volume fraction. The presence of a novel "1313" polymorph and competing R-P phases obscured proper identification of the phase for HTSC. Thus, achieving bulk HTSC and identifying the phase at play are the most prominent tasks at present. Here, we address these issues in the praseodymium (Pr)-doped La2PrNi2O7 polycrystalline samples. We find that the substitutions of Pr for La effectively inhibits the intergrowth of different R-P phases, resulting in nearly pure bilayer structure. For La2PrNi2O7, pressure-induced orthorhombic-to-tetragonal structural transition takes place at Pc ~ 11 GPa, above which HTSC emerges gradually upon further compression. The superconducting transition temperatures at 18-20 GPa reach Tconset = 82.5 K and Tczero = 60 K, which are the highest values among known nickelate superconductors. More importantly, bulk HTSC was testified by detecting clear diamagnetic signals below ~75 K corresponding to an estimated superconducting volume fraction ~ 57(5)% at 20 GPa. Our results not only resolve the existing controversies but also illuminate directions for exploring bulk HTSC in the bilayer nickelates.

Superconductivity,Strongly Correlated Electrons

What problem does this paper attempt to address?

The key problems that this paper attempts to solve include:

1. **Achieving Bulk High - Temperature Superconductivity (Bulk HTSC)**:
- In the double - layer nickelate La₃Ni₂O₇, although signs of high - temperature superconductivity have been observed under high - pressure conditions, an obvious diamagnetic signal (i.e., another important characteristic of superconductors) is still lacking. This is because the superconducting volume fraction in the sample is low and there is filamentary superconductivity.
- By introducing praseodymium (Pr) to replace lanthanum (La), the paper prepared La₂PrNi₂O₇ polycrystalline samples, which effectively suppressed the intergrowth between different Ruddlesden - Popper (R - P) phases, thus achieving a relatively pure double - layer structure. This enables the observation of an obvious diamagnetic signal under high - pressure conditions, proving the existence of bulk high - temperature superconductivity.

2. **Identifying the Phase Leading to High - Temperature Superconductivity**:
- In previous studies, due to the existence of the new "1313" polymorph and competing R - P phases, it was difficult to correctly identify the specific phase leading to high - temperature superconductivity.
- By studying La₂PrNi₂O₇ samples, the authors found that at a pressure of about 11 GPa, the structural transformation from the orthorhombic phase to the tetragonal phase promotes the emergence of high - temperature superconductivity. Under a pressure of 18 - 20 GPa, the superconducting transition temperature reaches Tc onset = 82.5 K and Tc zero = 60 K, which are the highest values among known nickelate superconductors.

3. **Verifying the Bulk Material Properties of High - Temperature Superconductivity**:
- To further verify the bulk material properties of high - temperature superconductivity, the authors estimated the superconducting volume fraction to be about 57(5)% by detecting an obvious diamagnetic signal below about 75 K, indicating that under a pressure of 20 GPa, La₂PrNi₂O₇ does exhibit the characteristics of bulk high - temperature superconductivity.

In summary, the main purpose of this paper is to solve the problems of achieving bulk high - temperature superconductivity in the double - layer nickelate La₃Ni₂O₇ and identifying its phase by improving the purity and structure of the sample, and finally successfully achieving bulk high - temperature superconductivity in La₂PrNi₂O₇, providing an ideal platform for future research on the high - temperature superconductivity mechanism of double - layer nickelates.