Role of coupled electrochemistry and stress on the Li-anode instability: A continuum approach

Shabnam Konica,Brian W. Sheldon,Vikas Srivastava

2024-05-09

Abstract:We present a coupled mechanistic approach that elucidates the intricate interplay between stress and electrochemistry, enabling the prediction of the onset of instabilities in Li-metal anodes and the solid electrolyte interphase (SEI) in liquid-electrolyte Li-metal batteries. Our continuum theory considers a two-way coupling between stress and electrochemistry, includes Li and electron transport through SEI, incorporates effects of Li viscoplasticity, includes SEI and electrolyte interface surface energy and evaluates crucial roles of these mechanistic effects on the continuously evolving anode surface due to the viscoplastic deformation of lithium. In the model, spatial current density evolves with the stress-induced potential across the deformed anode/SEI interface. We assume SEI as a homogeneous, artificial layer on the Li-anode, which allows the investigation of the mechanical and electrochemical properties of the SEI systematically. Subsequently, we solve a set of coupled electrochemistry and displacement equations within the SEI and anode domains. The model is implemented numerically by writing a user element subroutine in Abaqus/Standard. We conduct numerical simulations under various galvanostatic conditions and SEI properties and predict conditions for anode instability. We find that Li viscoplasticity is one of the key attributes that drives instability in the Li-anode and show that applying a soft artificial SEI layer on the Li-anode to minimize viscoplastic deformation can be an effective method. We also report the role of artificial SEI elasticity and thickness on anode stability. Selected stability maps are provided as a design aid for artificial SEI.

Numerical Analysis

What problem does this paper attempt to address?

The paper attempts to address the issue of the instability mechanisms of lithium metal anodes in liquid electrolyte lithium metal batteries. Specifically, the study focuses on how the interaction between stress and electrochemistry affects the stability of the lithium metal anode (Li-anode) and the solid electrolyte interphase (SEI) layer. The paper proposes a continuum approach that couples stress and electrochemistry to predict the onset conditions of instability in the lithium metal anode and SEI layer.

### Main Research Questions:
1. **Instability of Lithium Metal Anode**: During charge and discharge cycles, the lithium metal anode experiences uncontrollable dendrite growth, dead lithium formation, cracking, and SEI layer regrowth, which lead to battery performance degradation and potential safety hazards.
2. **Coupling Effect of Stress and Electrochemistry**: The local large volume changes of lithium metal and the SEI layer during plating and stripping cause SEI layer cracking, lithium metal creep, and low yield strength, leading to irreversible surface evolution. These phenomena indicate that mechanical factors play a crucial role in the failure of lithium metal batteries.
3. **Role of Artificial SEI Layer**: The study explores the impact of the elasticity, thickness, and surface energy of the artificial SEI layer on the stability of the lithium metal anode and how optimizing the SEI layer design can enhance battery stability.

### Research Methods:
- **Continuum Theory**: The paper proposes a continuum model that couples stress and electrochemistry, considering multiple factors such as lithium ion and electron transport in the SEI layer, viscoplastic deformation of lithium metal, and surface energy at the SEI layer and electrolyte interface.
- **Numerical Simulation**: Numerical simulations were conducted by writing user element subroutines in Abaqus/Standard to study the conditions of anode instability under different current densities and SEI layer properties.

### Key Findings:
- **Viscoplasticity of Lithium Metal as a Major Driver of Instability**: The study shows that the viscoplastic deformation of lithium metal is one of the key factors leading to anode instability.
- **Soft Artificial SEI Layer Can Effectively Reduce Viscoplastic Deformation**: Applying a soft artificial SEI layer can minimize the viscoplastic deformation of lithium metal, thereby enhancing anode stability.
- **Elasticity and Thickness of SEI Layer Have Significant Impact on Stability**: The paper provides stability maps showing the conditions of anode stability under different SEI layer properties, offering guidance for the design of artificial SEI layers.

### Conclusion:
By coupling stress and electrochemistry in a continuum model, the paper delves into the instability mechanisms of the lithium metal anode and SEI layer and proposes methods to enhance battery stability through optimized SEI layer design. These findings provide an important theoretical foundation for the future design and optimization of lithium metal batteries.