Vacancy diffusion barrier spectrum and diffusion correlation in multicomponent alloys
Bin Xing,Wanjuan Zou,Timothy J. Rupert,Penghui Cao
DOI: https://doi.org/10.1016/j.actamat.2024.119653
IF: 9.4
2024-01-07
Acta Materialia
Abstract:Vacancy diffusion serves a crucial role in many important kinetic behaviors and properties of multicomponent alloys. Essential questions, however, persist regarding how chemical complexity affects diffusion and what unique characteristics, if any, set these alloys apart from traditional metals. Using neural network-based kinetic Monte Carlo simulations, we study vacancy diffusion in multicomponent Nb-Mo-Ta alloys across a broad temperature range (2600 to 800 K). Unlike pure metals, the two key diffusion parameters—diffusion correlation factor f and activation energy ΔGm —are not constant in these alloys, but instead substantially decrease with decreasing temperature. This temperature dependence arises from fewer active vacancy jump pathways at lower temperatures, leading to more correlated jumps. Upon examining vacancy diffusion throughout the entire compositional space of the Nb-Mo-Ta alloy, we discover that the slowest vacancy diffusion surprisingly occurs in the non-equimolar region, rather than the equimolar concentration where the configurational entropy is highest. The inherent diffusion barrier spectrum, characterizing the diffusion energy landscape, controls both f and ΔGm and, thereby, the diffusivity. Finally, we find that the vacancy diffusion rate drops noticeably in the presence of local chemical order in the NbMoTa system, particularly for MoTa alloys with long-range B2 order.
materials science, multidisciplinary,metallurgy & metallurgical engineering