Abstract:The current geometric increase in the global deployment of solar photovoltaic (PV) modules, both at utility-scale and residential roof-top systems, is majorly attributed to its affordability, scalability, long-term warranty and, most importantly, the continuous reduction in the levelized cost of electricity (LCOE) of solar PV in numerous countries. In addition, PV deployment is expected to continue this growth trend as energy portfolio globally shifts towards cleaner energy technologies. However, irrespective of the PV module type/material and component technology, the modules are exposed to a wide range of environmental conditions during outdoor deployment. Oftentimes, these environmental conditions are extreme for the modules and subject them to harsh chemical, photo-chemical and thermo-mechanical stress. Asides from manufacturing defects, these conditions contribute immensely to PV module's aging rate, defects and degradation. Therefore, in recent times, there has been various investigations into PV reliability and degradation mechanisms. These studies do not only provide insight on how PV module's performance degrades over time, but more importantly, they serve as meaningful input information for future developments in PV technologies, as well as performance prediction for better financial modelling. In view of this, prompt and efficient detection and classification of degradation modes and mechanisms due to manufacturing imperfections and field conditions are of great importance towards minimizing potential failure and associated risks. In the literature, several methods, ranging from visual inspection, electrical parameter measurements (EPM), imaging methods, and most recently data-driven techniques have been proposed and utilized to measure or characterize PV module degradation signatures and mechanisms/pathways. In this paper, we present a critical review of recent studies whereby solar PV systems performance reliability and degradation were analyzed. The aim is to make cogent contributions to the state-of-the-art, identify various critical issues and propose thoughtful ideas for future studies particularly in the area of data- driven analytics. In contrast with statistical and visual inspection approaches that tend to be time consuming and require huge human expertise, data-driven analytic methods including machine learning (ML) and deep learning (DL) models have impressive computational capacities to process voluminous data, with vast features, with reduced computation time. Thus, they can be deployed for assessing module performance in laboratories, manufacturing, and field deployments. With the huge size of PV modules' installations especially in utility scale systems, coupled with the voluminous datasets generated in terms of EPM and imaging data features, ML and DL can learn irregular patterns and make conclusions in the prediction, diagnosis and classification of PV degradation signatures, with reduced computation time. Analysis and comparison of different models proposed for solar PV degradation are critically reviewed, in terms of the methodologies, characterization techniques, datasets, feature extraction mechanisms, accelerated testing procedures and classification procedures. Finally, we briefly highlight research gaps and summarize some recommendations for the future studies.

Analyzing the Impact of Design Factors on Solar Module Thermomechanical Durability Using Interpretable Machine Learning Techniques

Reliability-driven design optimization of si solar module under thermal cycling

Life Prediction of Solder Interconnects under Harsh Thermal Cycling from Microstructural Degradation

Comparative analysis of design optimization schemes for improving efficiency, durability and cost effectiveness in solar panels

Predicting encapsulant delamination in photovoltaic modules bridging photochemical reaction kinetics and fracture mechanics

Solar Photovoltaic Modules' Performance Reliability and Degradation Analysis—A Review

Physics-of-degradation-based life prediction of solder interconnects of long-life solar arrays in low-earth orbit

Understanding Photovoltaic Module Degradation: An Overview of Critical Factors, Models, and Reliability Enhancement Methods

Hybrid Data-Driven and Mechanistic Modeling Approach for Power Module Rapid Thermal Analysis

Comprehensive analysis of aging mechanisms and design solutions for desert-resilient photovoltaic modules

Understanding Causalities in Organic Photovoltaics Device Degradation in a Machine-Learning-Driven High-Throughput Platform

Comparing Hyper-optimized Machine Learning Models for Predicting Efficiency Degradation in Organic Solar Cells

Statistical Analysis and Structure Optimization of Large Photovoltaic Module

Prediction of structural mechanical properties of energy-saving materials for solar photovoltaic photo-thermal system based on deep learning

Unveiling the performance impact of module level features on parallel-connected lithium-ion cells via explainable machine learning techniques on a full factorial design of experiments

PV Modules and Their Backsheets -- A Case Study of a Multi-MW PV Power Station

From performance measurements to molecular level characterization: Exploring the differences between UV and DH weathering of PV modules

Long-term impact of light- and elevated temperature-induced degradation on photovoltaic arrays

Machine Learning Approach to Delineate the Impact of Material Properties on Solar Cell Device Physics.

Encapsulation strategies for mechanical impact and damp heat reliability improvement of lightweight photovoltaic modules towards vehicle-integrated applications

In-Situ Self-Monitoring of Real-Time Photovoltaic Degradation Only Using Maximum Power Point: the Suns-Vmp Method