Microwave magnetic excitations in U-type hexaferrite Sr$_4$CoZnFe$_{36}$O$_{60}$ ceramics

M. Kempa,V. Bovtun,D. Repček,J. Buršík,C. Kadlec,S. Kamba

2024-08-07

Abstract:Microwave (MW) transmission, absorption, and reflection loss spectra of the ferrimagnetic U-type hexaferrite Sr$_4$CoZnFe$_{36}$O$_{60}$ ceramics were studied from 100 MHz to 35 GHz at temperatures between 10 and 390 K. 9 MW magnetic excitations with anomalous behavior near the ferrimagnetic phase transitions were revealed. They also change under the application of weak bias magnetic field (0 - 700 Oe) at room temperature. 6 pure magnetic modes are assigned to dynamics of the magnetic domain walls and inhomogeneous magnetic structure of the ceramics, to the natural ferromagnetic resonance (FMR) and to the higher-frequency magnons. Three modes are considered as the magnetodielectric ones with dominating influence of the magnetic properties on their temperature and field dependences. Presence of the natural FMR in all ferrimagnetic phases proves existence of the non-zero internal magnetization and magnetocrystalline anisotropy. Splitting of the FMR into the two components without magnetic bias was observed in the collinear phase and is attributed to a change of the magnetocrystalline anisotropy during the phase transition. The high-frequency FMR component critically slows down to the phase transition. At room temperature, the FMR splitting and essential suppression of the higher-frequency modes was revealed under the weak bias field (300 - 700 Oe). The highly nonlinear MW response and the FMR splitting are caused by the gradual evolution of the polydomain magnetic structure to a monodomain one. The high number of magnetic excitations observed in the MW region confirms the suitability of using hexaferrite Sr$_4$CoZnFe$_{36}$O$_{60}$ ceramics as MW absorbers, shielding materials and highly tunable filters.

Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to study the magnetic excitation characteristics of U - type hexagonal ferrite Sr4CoZnFe36O60 ceramics in the microwave frequency band (100 MHz to 35 GHz), especially the behavior under different temperatures (10 K to 390 K) and weak bias magnetic fields (0 - 700 Oe). Specifically, the paper focuses on the following aspects:

1. **Abnormal behavior of magnetic excitation**: Nine kinds of microwave magnetic excitations were studied, and these excitations showed abnormal behavior near the ferromagnetic phase transition, especially the changes when a weak bias magnetic field was applied at room temperature.

2. **Identification of pure magnetic modes**: Six pure magnetic modes were determined, and these modes are related to the dynamics of magnetic domain walls, inhomogeneous magnetic structures, natural ferromagnetic resonance (FMR), and high - frequency magnons.

3. **Analysis of magnetodielectric modes**: Three excitations considered as magnetodielectric modes were explored, and the temperature and magnetic field dependence of these modes are mainly affected by magnetic properties.

4. **Existence of natural ferromagnetic resonance (FMR)**: By observing the existence of natural FMR, the existence of non - zero magnetization and magnetocrystalline anisotropy inside the material was proved.

5. **FMR splitting phenomenon**: In the collinear phase, the natural FMR was observed to split into two components, which was attributed to the change of magnetocrystalline anisotropy during the phase transition. The FMR component in the high - frequency band slowed down significantly near the critical point of the phase transition.

6. **Effect of weak bias magnetic field**: When a weak bias magnetic field (300 - 700 Oe) was applied at room temperature, FMR splitting and significant suppression of the high - frequency mode were observed.

7. **Evolution of multi - domain magnetic structure**: The highly nonlinear microwave response and FMR splitting were caused by the gradual evolution of the multi - domain magnetic structure into a single - domain structure.

8. **Application potential of the material**: The research results show the application potential of U - type hexagonal ferrite Sr4CoZnFe36O60 ceramics in microwave absorption, shielding materials, and highly tunable filters.

Through these studies, the paper aims to deeply understand the magnetic excitation characteristics and potential applications of U - type hexagonal ferrite Sr4CoZnFe36O60 ceramics in the microwave frequency band.