Polymer Coating with Balanced Coordination Strength and Ion Conductivity for Dendrite‐Free Zinc Anode

Xiaomin Cai,Wenzhi Tian,Zekai Zhang,Yan Sun,Lei Yang,Hongchun Mu,Cheng Lian,Huibin Qiu

DOI: https://doi.org/10.1002/adma.202307727

IF: 29.4

2023-10-13

Advanced Materials

Abstract:Decorating Zn anodes with functionalized polymers has been considered as an effective strategy to inhibit dendrite growth. However, this normally brings extra interfacial resistance rendering slow reaction kinetics of Zn2+. Herein, we report a poly(2‐vinylpyridine) (P2VP) coating with modulated coordination strength and ion conductivity for dendrite‐free Zn anode. The P2VP coating favors a high electrolyte wettability and rapid Zn2+ migration speed (Zn2+ transfer number, tZn2+ = 0.58). Electrostatic potential calculation shows that P2VP mildly coordinates with Zn2+ (adsorption energy = ‐0.94 eV), which promotes a preferential deposition of Zn along the (002) crystal plane. Notably, the use of partially (26%) quaternized P2VP (q‐P2VP), further reduces the interfacial resistance to 126 Ω, leading to a high ion migration speed (tZn2+ = 0.78) and a considerably low nucleation overpotential (18 mV). As a result of the synergistic effect of mild coordination and partial electrolysis, the overpotential of the q‐P2VP‐decorated Zn anode retains at a considerably low level (∼46 mV) over 1000 h at a high current density of 10 mA cm−2. The assembled (NH4)2V6O16·1.5H2O || glass fiber || q‐P2VP‐Zn full cell reveals a lower average capacity decay rate of only 0.018% per cycle within 500 cycles at 1 A g−1. This article is protected by copyright. All rights reserved

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology