Structural and magnetic properties of molecular beam epitaxy (MnSb2Te4)x(Sb2Te3)1-x topological materials with exceedingly high Curie temperature

Candice R. Forrester,Christophe Testelin,Kaushini Wickramasinghe,Ido Levy,Dominique Demaille,David Hrabovski,Xiaxin Ding,Lia Krusin-Elbaum,Gustavo E. Lopez,Maria C. Tamargo

2023-11-18

Abstract:Tuning magnetic properties of magnetic topological materials is of interest to realize elusive physical phenomena such as quantum anomalous hall effect (QAHE) at higher temperatures and design topological spintronic devices. However, current topological materials exhibit Curie temperature (TC) values far below room temperature. In recent years, significant progress has been made to control and optimize TC, particularly through defect engineering of these structures. Most recently we showed evidence of TC values up to 80K for (MnSb2Te4)x(Sb2Te3)1-x, where x is greater than or equal to 0.7 and less than or equal to 0.85, by controlling the compositions and Mn content in these structures. Here we show further enhancement of the TC, as high as 100K, by maintaining high Mn content and reducing the growth rate from 0.9 nm/min to 0.5 nm/min. Derivative curves reveal the presence of two TC components contributing to the overall value and propose TC1 and TC2 have distinct origins: excess Mn in SLs and Mn in Sb2-yMnyTe3QLs alloys, respectively. In pursuit of elucidating the mechanisms promoting higher Curie temperature values in this system, we show evidence of structural disorder where Mn is occupying not only Sb sites but also Te sites, providing evidence of significant excess Mn and a new crystal structure:(Mn1+ySb2-yTe4)x(Sb2-yMnyTe3)1-x. Our work shows progress in understanding how to control magnetic defects to enhance desired magnetic properties and the mechanism promoting these high TC in magnetic topological materials such as (Mn1+ySb2-yTe4)x(Sb2-yMnyTe3)1-x.

Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is how to increase the Curie temperature (\(T_C\)) of the magnetic topological material \((\text{MnSb}_2\text{Te}_4)_x(\text{Sb}_2\text{Te}_3)_{1 - x}\) by adjusting the growth parameters. Specifically, the researchers focus on how to achieve higher \(T_C\) values by controlling the manganese content in the material and reducing the growth rate, thus making it possible to realize the quantum anomalous Hall effect (QAHE) and design topological spintronic devices. Currently, the \(T_C\) values of topological materials are far below room temperature, which limits their potential in practical applications. Therefore, this research aims to significantly increase the \(T_C\) value by optimizing the growth conditions of the material, especially by reducing the growth rate and increasing the manganese content, so that it approaches or exceeds 100K, thereby promoting the application research of these materials at higher temperatures.