Sieving and clogging in PEG-PEGDA hydrogel membranes

Malak Alaa Eddine,Alain Carvalho,M. Schmutz,Thomas Salez,Sixtine de Chateauneuf-Randon,Bruno Bresson,S. Belbekhouche,C. Monteux

2023-10-06

Abstract:Hydrogels are promising systems for separation applications due to their structural characteristics (i.e. hydrophilicity and porosity). In our study, we investigate the permeation of suspensions of rigid latex particles of different sizes through free-standing hydrogel membranes prepared by photopolymerization of a mixture of poly (ethylene glycol) diacrylate (PEGDA) and large poly (ethylene glycol) (PEG) chains of 300 000 g.mol-1 in the presence of a photoinitiator. Atomic force microscopy (AFM) and cryoscanning electron microscopy (cryoSEM) were employed to characterize the structure of the hydrogel membranes. We find that the 20 nm particle permeation depends on both the PEGDA/PEG composition and the pressure applied during filtration. In contrast, we do not measure a significant permeation of the 100 nm and 1 $\mu$m particles, despite the presence of large cavities of 1 $\mu$m evidenced by cryoSEM images. We suggest that the PEG chains induce local nanoscale defects in the cross-linking of PEGDA-rich walls separating the micron size cavities, that control the permeation of particles and water. Moreover, we discuss the decline of the permeation flux observed in the presence of latex particles, compared to that of pure water. We suggest that a thin layer of particles forms on the surface of the hydrogels.

Soft Condensed Matter

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to study the permeation behavior of rigid latex particles of different sizes (20 nm, 100 nm and 1 μm) when passing through a composite hydrogel membrane of polyethylene glycol diacrylate (PEGDA) and high - molecular - weight polyethylene glycol (PEG). Specifically, the research focuses on the following aspects:

1. **Permeability of water and particles**: Explore how the permeability of water and particles of different sizes through the hydrogel membrane is affected by pressure and hydrogel composition. The study found that the permeability of 20 - nm particles depends on the ratio of PEGDA/PEG and the applied pressure, while the permeabilities of 100 - nm and 1 - μm particles are significantly lower, even in the presence of large micron - sized cavities in the hydrogel.

2. **Effect of hydrogel structure on permeability**: Characterize the structure of the hydrogel membrane by atomic force microscopy (AFM) and cryogenic scanning electron microscopy (cryo - SEM), and explore how the microstructure of the hydrogel affects the permeation behavior of particles and water. The study found that PEG chains induce local nanoscale defects on the cross - linking walls in PEGDA - rich regions, and these defects control the permeation of particles and water.

3. **Particle clogging phenomenon**: Discuss the phenomenon of permeability decline due to the formation of a thin layer of particles on the surface of the hydrogel during the filtration process. The study found that for 100 - nm particles, this clogging is irreversible, while for 1 - μm particles, the clogging is reversible, and these large particles do not enter the interior of the hydrogel.

4. **Effect of pressure on permeation behavior**: Study the permeation behavior of particles under different pressures, and find that pressure has a significant effect on the permeation of 20 - nm particles, and at low pressures (such as 2 KPa), 20 - nm particles hardly permeate. This may be because the hydrogel is a soft material and will deform at higher pressures, allowing particles to pass through.

In summary, this paper aims to deeply understand the screening and clogging mechanisms of PEGDA/PEG hydrogel membranes for particles of different sizes during the filtration process through experimental and characterization means, and provide a theoretical basis for designing more effective filtration materials.