Abstract:Spatially resolved information on corrosion reactions operating at the cut edges of coated metals can be obtained using microelectrochemical scanning techniques using a suitable selection of operation modes and scanning probes. The scanning vibrating electrode technique (SVET) provides current density maps with a spatial resolution of the order of the dimensions of the sample, which allows the temporal evolution of the corrosion reactions to be followed over time. This leads to the identification and localization of cathodic and anodic sites, although the technique lacks chemical specificity for the unequivocal identification of the reactive species. The application of scanning electrochemical microscopy (SECM) was previously limited to image cathodic reaction sites, either due to oxygen consumption in the amperometric operation or by the alkalinisation of the electrolyte in potentiometric operation. However, it is shown that anodic sites can be effectively monitored using an ion-selective microelectrode (ISME) as a probe. The ISME probes detected differences in the local concentrations of Zn2+ and OH- ions from the cut edges of a complete coil coating system compared to the same system after the polymeric layers were removed. In this way, it has been shown that the inhibitor loading in the polymer layers effectively contributes to reducing the corrosion rates at the cut edge, thus helping to extend the useful life of the sacrificial galvanized layer bonded directly to the steel matrix. Additionally, these two probe configurations can be integrated into a multi-electrode tip for potentiometric operation to simultaneously monitor localized changes in pH values and metal ion dissolution in a single scan. Spatial and temporal distributions were further investigated using different rastering procedures, and the potential of constructing pseudomaps for 2D-imaging is described.

Nondestructive detection and quantification of localized corrosion rates by electrochemical tomography

A novel electrical resistance tomography system based on C4D technique

A Novel Electrical Resistance Tomography System Based on ${\rm{c}}^{4}{\rm D}$ Technique

An Electrochemical Method for Measuring Localized Corrosion under Cathodic Protection

Quantitative Nondestructive Estimation of Deep Defects in Conductive Structures

Smart Cathodic Protection System for Real-Time Quantitative Assessment of Corrosion of Sacrificial Anode Based on Electro-Mechanical Impedance (EMI)

Eddy Current Pulsed Thermography for Steel Corrosion Characterization

Corrosion Damages of Reinforced Concrete Characterized by X-ray CT and DVC Techniques

Development of an electrochemistry-based corrosion sensor to monitor corrosion of boiler tubes, pipes, and painted structures

Multiphysics Structured Eddy Current and Thermography Defects Diagnostics System in Moving Mode.

Contributions of Microelectrochemical Scanning Techniques for the Efficient Detection of Localized Corrosion Processes at the Cut Edges of Polymer-Coated Galvanized Steel

Pulse-Modulation Eddy Current Imaging for 3D Profile Reconstruction of Subsurface Corrosion in Metallic Structures of Aviation

Early corrosion detection in structural carbon steels using electromagnetic sensors

Detection and Sizing of Defects in Structural Components of A Nuclear Power Plant by Ect

Microscale chemical imaging to characterize and quantify corrosion processes at the metal-electrolyte interface

Nondestructive Eddy Current Array (ECA) Technique for Stress Corrosion Cracking (SCC) Detection and Assessment

Application of EIS to localized corrosion

Detection of corrosion under insulation on aerospace structures via pulsed eddy current thermography

Quantitative Evaluation of Electrical Conductivity Inside Stress Corrosion Crack with Electromagnetic NDE Methods

Quantitative NDE of Cellular Metallic Materials and Structures by Using Eddy Current Testing Technique