Independent characterization of the elastic and the mixing parts of hydrogel osmotic pressure

Zefan Shao,Qihan Liu

2023-09-15

Abstract:Osmotic pressure is the driving force for the swelling of hydrogels. The hydrogel osmotic pressure can be decomposed into two parts: the mixing part due to polymer-solvent interaction and the elastic part due to polymer chain stretching. While the two components are distinguished in existing constitutive models, they have not been independently characterized in experiments. This paper reports a novel method to independently measure these two components using a fully constrained swelling test. The test allows the crosslink density to be varied at a fixed polymer content, thus varying the elastic part independently of the mixing part. Our measurement shows that the widely used Flory-Rehner model predicts the mixing part accurately for polyacrylamide hydrogel of a wide range of swelling ratios but predicts the elastic part with orders-of-magnitude error.

Soft Condensed Matter

What problem does this paper attempt to address?

The paper attempts to address the issue of independently characterizing the mixing part and the elastic part in the osmotic pressure of hydrogels. Specifically, existing theoretical models (such as the Flory-Rehner model) distinguish between these two parts, but they cannot be independently measured in experiments. Therefore, the paper proposes a novel fully constrained swelling test method that can measure these two parts separately.

The study found that when the crosslinking density is sufficiently low, the osmotic pressure is mainly dominated by the mixing part and is independent of elasticity. Through this method, the elastic part at different crosslinking densities can be independently determined. Experimental results show that for polyacrylamide hydrogels, within a wide range of polymer content (0.07 ≤ 𝜙 ≤ 0.51), the mixing part can be well explained by the classical Flory-Rehner model, but the elastic part has an order of magnitude error. This research provides a new direction for developing more accurate constitutive models for hydrogels.