Abstract:Ever since hydrogen-based superconductors have been actively considered as candidates for room-temperature superconductors, binary hydrides have been almost completely explored theoretically. Now researchers are turning their interest to ternary hydrides. However, the enormous compositional and structural possibilities in the ternary hydride space limit the search efficiency. Here, using an advanced crystal structure search method combined with first-principles calculations, a series of ternary hydrides AXH 6 (MgPH 6 , MgAsH 6 , CaSbH 6 , CaSnH 6 , NaSbH 6 and ScSiH 6 ) with the A15-type structure are predicted to be stable at around one million atmospheres. Among them, CaSnH 6 presents the lowest thermodynamically stable pressure of 110 GPa. CaSbH 6 , CaSnH 6 and ScSiH 6 may be dynamically stable down to 41 (70), 71 (90) and 86 (70) GPa, respectively, without (with) anharmonic effects and temperature effects. Hydrogen atoms in these A15-type structures are found to form weak covalent bonds to X atoms. More interestingly, we find that ternary hydrides with the AXH 6 stoichiometry may assume the A15-type structure under pressure when the sum of the chemical valences of the two non-hydrogen atoms is six or seven. Based on electron-phonon coupling calculations, all these ternary hydrides are estimated to be superconductors. CaSbH 6 , CaSnH 6 and ScSiH 6 have superconducting transition temperatures ( T c s) of 65, 53 and 116 K at 45, 75 and 90 GPa, respectively, while MgPH 6 has the highest T c of 148 K at 135 GPa. Our study will provide guidance for designing high T c ternary hydrides near ambient pressures.

High-temperature superconductivity in A15-type La4H23 below 100 GPa

Unusual metallic state in superconducting A15-type La4H23

Large negative magnetoresistance and pseudogap phase in superconducting A15-type La$_4$H$_{23}$

(La,Th)H 10 : Potential High- T c (242 K) Superconductors Stabilized Thermodynamically below 200 GPa

Hot Hydride Superconductivity above 550 K

Synthesis of superconducting phase of La0.5Ce0.5H10at high pressures

Prediction of high- T c superconductivity in ternary lanthanum borohydrides

Enhancement of the superconducting critical temperature realized in the La-Ce-H system at moderate pressures

Evidence for superconductivity above 260 K in lanthanum superhydride at megabar pressures

Superconductivity at 215 K in lanthanum hydride at high pressures

Few-Hydrogen High- T c Superconductivity in (Be 4 ) 2 H Nanosuperlattice with Promising Ductility under Ambient Pressure

High-temperature Superconductivities and Crucial Factors Influencing Stability of LaThH12 under Moderate Pressures

A-15 type superconducting hydride $La_4H_{23}$: Nanograined structure with low strain, strong electron-phonon interaction, and moderate level of nonadiabaticity

Pressure-induced hydride superconductors above 200 K

Designing ternary superconducting hydrides with A15-type structure at moderate pressures

Few-Hydrogen High-Tc Superconductivity in (be4)2h Nanosuperlattice with Promising Ductility under Ambient Pressure.

High-temperature superconductivity up to 223 K in the Al stabilized metastable hexagonal lanthanum superhydride

High-temperature superconductivity on the verge of a structural instability in lanthanum superhydride

Computational Materials Discovery for Lanthanide Hydrides at high pressure: predicting High Temperature superconductivity

Superconductivity in hexagonal Ce La H under high pressure

High temperature superconductivity of quaternary hydrides XM3Be4H32 (X, M = Ca, Sr, Ba, Y, La, Ac, Th) under moderate pressure