Gd-Based Solvated Shells for Defect Passivation of CsPbBr$_3$ Nanoplatelets Enabling Efficient Color-Saturated Blue Electroluminescence

Haoran Wang,Jingyu Qian,Jiayun Sun,Tong Su,Shiming Lei,Xiaoyu Zhang,Wallace C. H. Choy,Xiao Wei Sun,Kai Wang,Weiwei Zhao

2023-06-24

Abstract:Reduced-dimensional CsPbBr$_3$ nanoplatelets (NPLs) are promising candidates for color-saturated blue emitters, yet their electroluminescence performance is hampered by non-radiative recombination, which is associated with bromine vacancies. Here, we show that a post-synthetic treatment of CsPbBr$_3$ NPLs with GdBr$_3$-dimethylformamide (DMF) can effectively eliminate defects while preserving the color. According to a combined experimental and theoretical study, Gd$^{3+}$ ions are less reactive with NPLs as a result of compact interaction between them and DMF, and this stable Gd$^{3+}$-DMF solvation structure makes Brions more available and allows them to move more freely. Consequently, defects are rapidly passivated and photoluminescence quantum yield increases dramatically (from 35 to ~100%), while the surface ligand density and emission color remain unchanged. The result is a remarkable electroluminescence efficiency of 2.4% (at 464 nm), one of the highest in pure blue perovskite NPL light-emitting diodes. It is noteworthy that the conductive NPL film shows a high photoluminescence quantum yield of 80%, demonstrating NPLs' significant electroluminescence potential with further device structure design.

Applied Physics,Materials Science

What problem does this paper attempt to address?

This paper mainly discusses how to solve the problem of non-radiative recombination caused by bromine vacancies in pure blue perovskite nanoplates (CsPbBr3 Nanoplatelets) in terms of electroluminescence (EL) performance. The researchers effectively eliminated defects and maintained color stability by post-synthetic treatment using GdBr3 (gadolinium bromide) and dimethylformamide (DMF) solution to treat CsPbBr3 nanoplates. Experimental and theoretical studies have shown that the close interaction between Gd3+ ions and DMF molecules prevents Gd3+ from reacting with the nanoplate surface, allowing Br- ions to move freely and quickly repair surface defects, significantly improving the photoluminescence quantum yield (PLQY) from 35% to nearly 100%. As a result, a high external quantum efficiency (EQE) of 2.4% has been achieved, which is one of the highest values in pure blue perovskite LEDs based on NPLs. The study also found that NPLs treated with GdBr3 can maintain good charge transport properties while maintaining high PLQY compared to treatment with NaBr and ZnBr2. These findings provide a new strategy for improving the light emitting efficiency of perovskite nanoplates while preserving their electrical properties.