Vadym Iurchuk,Oleksii Kozlov,Serhii Sorokin,Shengqiang Zhou,Jürgen Lindner,Serhii Reshetniak,Anatolii Kravets,Dmytro Polishchuk,Vladislav Korenivski
Abstract:We present all-electrical operation of a Fe$_x$Cr$_{1-x}$-based Curie switch at room temperature. More specifically, we study the current-induced thermally-driven transition from ferromagnetic to antiferromagnetic Ruderman-Kittel-Kasuya-Yosida (RKKY) indirect coupling in a Fe/Cr/Fe$_{17.5}$Cr$_{82.5}$/Cr/Fe multilayer. Magnetometry measurements at different temperatures show that the transition from the ferromagnetic to the antiferromagnetic coupling at zero field is observed at $\sim$325K. Analytical modelling confirms that the observed temperature-dependent transition from indirect ferromagnetic to indirect antiferromangetic interlayer exchange coupling originates from the modification of the effective interlayer exchange constant through the ferromagnetic-to-paramagnetic transition in the Fe$_{17.5}$Cr$_{82.5}$ spacer with minor contributions from the thermally-driven variations of the magnetization and magnetic anisotropy of the Fe layers. Room-temperature current-in-plane magnetotransport measurements on the patterned Fe/Cr/Fe$_{17.5}$Cr$_{82.5}$/Cr/Fe strips show the transition from the 'low-resistance' parallel to the 'high-resistance' antiparallel remanent magnetization configuration, upon increased probing current density. Quantitative comparison of the switching fields, obtained by magnetometry and magnetotransport, confirms that the Joule heating is the main mechanism responsible for the observed current-induced resistive switching.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to achieve all - electric operation of the Curie switch based on Fe xCr1−x materials at room temperature. Specifically, the researchers aim to control the transition between ferromagnetic coupling and antiferromagnetic coupling in a multilayer magnetic structure through the current - driven Joule heating effect. The realization of this goal will provide a thermally - controlled magnetic transport method without an external magnetic field for spintronic devices (such as magnetic sensors, magnetoresistive random - access memory (MRAM), and spin - torque nano - oscillators (STNO)).
### Research Background and Problems
With the increasing demand for miniaturization in the field of spintronics, it is crucial to design and implement composite magnetic components that can respond to various external control parameters (such as electric fields, magnetic fields, temperatures, etc.). These components are regarded as the basic building blocks of emerging multi - functional spintronic devices. Among them, the interlayer exchange coupling (IEC) is the basis for the discovery of the giant magnetoresistance (GMR) phenomenon and is widely used in hard - disk read - write heads, opening up the research field of spintronics.
However, once the multilayer samples are prepared, it is not easy to adjust the IEC on demand. Changing the temperature of the multilayer materials can adjust the IEC intensity, which is one of the only reasonable external parameters. Another method is to use a specific spacer layer material with a Curie temperature close to room temperature. In this case, the thermally - induced transition from the ferromagnetic to the paramagnetic state will change the effective spacer layer thickness, thereby modifying the IEC.
### Research Content
This paper studies the thermally - controlled indirect IEC switching in the Fe/Cr/Fe 17.5Cr82.5/Cr/Fe multilayer structure. The main research contents include:
1. **Temperature - Dependent Vibrating - Sample Magnetometer (VSM) Measurements**: It shows the transition from ferromagnetic coupling to antiferromagnetic coupling in the multilayer structure at different temperatures, especially near the Curie temperature.
2. **Analytical Modeling**: Based on the principle of minimizing magnetic energy, it verifies that the observed transition is caused by the change in the temperature - dependent IEC constant, and secondary factors include thermally - related changes in magnetization and magnetic anisotropy.
3. **Current - In - Plane Magnetic Transport Measurements**: Through the measurement of patterned Fe/Cr/Fe 17.5Cr82.5/Cr/Fe strips, it confirms the current - driven reversible IEC control and shows the magnetoresistive switching in zero - field.
### Results and Discussions
The experimental results show that near the Curie temperature (about 325K), the Fe 17.5Cr82.5 spacer layer changes from the ferromagnetic state to the paramagnetic state, causing the multilayer structure to change from a low - resistance state (parallel magnetization) to a high - resistance state (antiparallel magnetization). Through the current - driven Joule heating effect, this transition can be achieved at room temperature. The results of hysteresis loops and magnetic transport measurements indicate that this transition is mainly caused by the change in the temperature - dependent IEC constant.
In addition, the analytical modeling further confirms that the temperature - dependent IEC change is the main mechanism, and the "loose spins" have a minor impact on the IEC. Finally, by fitting the experimental data, the relationship between the current density and the temperature is estimated, and the critical current density is determined to be approximately \( j_c = 1.39\times 10^{11}\, \text{A/m}^2 \), corresponding to the sample being heated to the Curie temperature of about 324K.
### Application Prospects
This research provides new possibilities for spintronic devices without magnetic - field control at room temperature. For example, by finely adjusting the Fe xCr1−x material parameters, the Curie temperature and the switching field can be optimized, thereby precisely adjusting the working temperature range and the required current density. In addition, this Curie switch can also be used for electrically - controlled conversion in magnetoresistive memory cells and as a composite free layer in spin - torque oscillators, introducing new space for dynamic tuning.
In summary, this research solves the problem of how to reversibly switch between ferromagnetic coupling and antiferromagnetic coupling in a multilayer magnetic structure at room temperature through current - driven means, providing new ideas and technical means for the design and application of spintronic devices.