Significant enhancement of critical current density in H+-intercalated FeSe single crystal

Yan Meng,Wei Wei,Xiangzhuo Xing,Xiaolei Yi,Nan Zhou,Yufeng Zhang,Wenhui Liu,Yue Sun,Zhixiang Shi
DOI: https://doi.org/10.1088/1361-6668/ac72cd
2023-03-21
Abstract:Superconducting transition temperature (Tc) and critical current density (Jc) are two key factors that are not only crucial for probing high-temperature superconducting mechanisms, but also for practical applications. The simple crystal structure of FeSe is very favorable for the fabrication of thin films and wires, but its application is limited by the relatively low Tc and small Jc. A previous study has found that the Tc of FeSe can be significantly enhanced over 40 K by using the protonation method. Here, we present a systematic study of Jc and vortex properties of H+-intercalated FeSe (Hx-FeSe) single crystals. The value of Jc for Hx-FeSe single crystal is significantly enhanced, exceeding 1.3*10^6 A/cm2 at 4 K, which is more than two orders of magnitude larger than 1.1*10^4 A/cm2 of pristine FeSe. The vortex pinning mechanism of Hx-FeSe is found to be surface pinning, which is different from the dominant strong point-like pinning in pristine FeSe. Moreover, the systematic study of the vortex phase transition and the underlying mechanism provides a wealth of information for the vortex phase diagram of Hx-FeSe single crystal. Our results confirm that the introduction of H+ intercalations into FeSe not only enhances the Tc, but also significantly increases the value of Jc, which is favorable for practical applications.
Superconductivity
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to significantly increase the critical current density (Jc) of iron - selenium (FeSe) single crystals through the proton intercalation (H+ intercalation) method. Specifically, the research focuses on the following aspects: 1. **Enhancing the critical current density**: Through the H+ intercalation method, the critical current density (Jc) of FeSe single crystals has been significantly improved. At 4K, the Jc value of Hx - FeSe exceeds 1.3×10^6 A/cm², which is two orders of magnitude higher than the Jc value (1.1×10^4 A/cm²) of untreated FeSe. 2. **Exploring the vortex - pinning mechanism**: The vortex - pinning mechanism in Hx - FeSe single crystals has been studied, and it has been found that it is mainly manifested as surface pinning, which is different from the strong point - like pinning that dominates in untreated FeSe. 3. **Research on the vortex - phase diagram**: The vortex - phase diagram of Hx - FeSe single crystals has been systematically studied, including the characteristics of different regions such as the vortex liquid - solid phase transition, the vortex glass state, and the vortex - sliding liquid state. 4. **Potential for high - temperature superconducting applications**: Through these studies, it has been verified that H+ intercalation not only increases the superconducting transition temperature (Tc) of FeSe, but also significantly enhances the critical current density (Jc), thus providing favorable conditions for practical applications. ### Main research content - **Experimental methods**: - High - quality FeSe single crystals were prepared and treated by the proton intercalation method. - Magnetic - transport and electrical - transport measurements were carried out using a Physical Properties Measurement System (PPMS - 9T). - **Results and discussion**: - **Resistivity and susceptibility**: The resistivity behavior of Hx - FeSe is different from that of untreated FeSe, indicating that proton intercalation has changed the electronic structure or scattering mechanism. The superconducting transition temperature (Tc) of Hx - FeSe is about 44K, much higher than about 9K of untreated FeSe. - **Hysteresis loop**: The Jc value was extracted from the magnetic hysteresis loop (MHL) by the extended Bean model, and the Jc value of Hx - FeSe is significantly higher than that of untreated FeSe. - **Vortex - pinning force**: Through the relationship between the normalized vortex - pinning force (f = Fp/Fp_max) and the normalized magnetic field (h = H/H_max), the vortex - pinning mechanism of Hx - FeSe was determined to be surface pinning. - **Vortex - phase diagram**: The vortex - phase diagram of Hx - FeSe single crystals was constructed, and the characteristics of the vortex liquid, the vortex - sliding liquid, and the vortex glass state at different temperatures and magnetic fields were described in detail. ### Conclusion Through the proton intercalation method, the critical current density (Jc) of Hx - FeSe single crystals has been significantly increased, and the vortex - pinning mechanism has also changed. These results not only help to understand the superconducting mechanism of iron - based superconductors, but also provide an important reference for the practical application of high - temperature superconducting materials.