Abstract:Inspired by the excellent activity of platinum in hydrogen evolution reaction (HER) and the good performance of Ni-based compounds in oxygen evolution reaction (OER), a bifunctional electrocatalyst PtNi carbon nanofiber (CNF) is designed and fabricated using electrospinning followed by carbonization. Ultra-small PtNi nanoparticles of several nanometers in size are densely dispersed on every CNF, along with a few larger nanoparticles with sizes of several decades of nanometers. The as-prepared catalysts can be directly used as an electrode and act as high-efficiency materials for water splitting, including HER and OER. For HER activity, the PtNi/CNFs reach 10 mA cm−2 current density at low overpotentials of 34 mV and exhibit a small Tafel slope of 31 mV dec−1 in acidic electrolytes of 0.5 M H2SO4, which is close to that of commercial Pt/C (20 wt%) electrocatalytic catalysts. In 1 M KOH solution, the PtNi/CNFs also exhibit excellent HER activity with a low overpotential of 82 mV to achieve a current density of 10 mA cm−2 and a small Tafel slope of 34 mV dec−1. Moreover, the PtNi/CNFs also show good activity for OER in alkaline electrolyte of 1 M KOH with a Tafel slope of 159 mV dec−1 and a small overpotential of 151 mV to reach a current density of 10 mA cm−2. In addition, the OER performance of the PtNi/CNFs in acid media is also favorable, with a 198 mV dec−1 Tafel slope. The decent activity of the PtNi/CNFs for water splitting originates from the synergistic effects of using Pt and Ni, large amounts of ultra-small nanoparticles densely dispersed on the CNFs, high conductivity of the support materials and interconnected three-dimensional structures of the carbon nanofiber mats.

Electrospun prussian blue analogue derived NiCo@N-doped carbon nanofibers as efficient and highly stable electrocatalysts for neutral overall water splitting

Nitrogen-doped Fe2O3/NiTe2 as an excellent bifunctional electrocatalyst for overall water splitting

Nitrogen-doped porous carbon encapsulated nickel iron alloy nanoparticles, one-step conversion synthesis for application as bifunctional catalyst for water electrolysis

Nitrogen-doped Fe<sub>2</sub>O<sub>3</sub>/NiTe<sub>2</sub> as an excellent bifunctional electrocatalyst for overall water splitting

NiCo layered double hydroxides derived Ni0.67Co0.33(PO3)2 as stable and efficient electrocatalysts for overall water splitting

Self-supporting Amorphous Nanoporous NiFeCoP Electrocatalyst for Efficient Overall Water Splitting

Anchoring Ni2P Sheets on NiCo2O4 Nanocone Arrays as Optimized Bifunctional Electrocatalyst for Water Splitting

Fabrication of NiC/MoC/NiMoO4 Heterostructured Nanorod Arrays as Stable Bifunctional Electrocatalysts for Efficient Overall Water Splitting

Mo,Fe-codoped metal phosphide nanosheets derived from Prussian blue analogues for efficient overall water splitting

N-doped Carbon Coated FeNiP Nanoparticles Based Hollow Microboxes for Overall Water Splitting in Alkaline Medium

Hierarchical core-shell structural Ni2P/NiMoO4 @CoP/FeP2 nanorods as difunctional electrocatalysts for efficient overall water splitting

A Bifunctional Electrocatalyst of PtNi Nanoparticles Immobilized on Three-Dimensional Carbon Nanofiber Mats for Efficient and Stable Water Splitting in Both Acid and Basic Media

Amorphous NiFe phosphides supported on nanoarray-structured nitrogen-doped carbon paper for high-performance overall water splitting

Partially Oxidized Ni Nanoparticles Supported on Ni-N Co-Doped Carbon Nanofibers As Bifunctional Electrocatalysts for Overall Water Splitting

FeNi alloy nanoparticles embedded in electrospun nitrogen-doped carbon fibers for efficient oxygen evolution reaction

<i>In situ</i> formation of NiCoP@phosphate nanocages as an efficient bifunctional electrocatalyst for overall water splitting

Double metal–organic frameworks derived Fe–Co–Ni phosphides nanosheets as high-performance electrocatalyst for alkaline electrochemical water splitting

Controllable preparation of N-doped Ni3S2 nanocubes@N-doped graphene-like carbon layers for highly active electrocatalytic overall water splitting

Self-supported electrode of NiCo-LDH/NiCo2S4/CC with enhanced performance for oxygen evolution reaction and hydrogen evolution reaction

Synergism of NiFe layered double hydroxides/phosphides and Co-NC nanorods array for efficient electrocatalytic water splitting

Integrated Bifunctional Electrodes Based on Amorphous Co-Ni-S Nanoflake Arrays with Atomic Dispersity of Active Sites for Overall Water Splitting.