Abstract:We propose a probabilistic model coupling with the temperature dependent constitutive relationship to describe the competition between the cleavage and ductile void failure of ferritic/martensitic steels with irradiation effects. It is found that both the material deformation and failure modes exhibit significant temperature dependence. Regarding the material deformation, two regimes have been found for the ductile-to-brittle transition (DBT). At low temperature, the flow stress is controlled by the mobility of screw dislocations. The high-temperature regime is about the thermally activated jog drag of dislocations. The failure modes depend on the carbide precipitate and temperature. Cleavage micro-cracks initiate at the carbide sites at low temperature giving rise to brittle behaviors. At high temperature, void nucleation evolving from the carbide precipitate suppresses the cleavage nucleation and propagation, and leads to good ductility. It is demonstrated that the competition between the cleavage fracture and ductile void failure is the major mechanism for the DBT. Our probabilistic model successfully predicts the temperature-dependent fracture toughness and ductile-to-brittle transition temperature (DBTT). Besides temperature, irradiation has a significant effect on the DBT of steels. Upon irradiation, the steels exhibit both irradiation hardening and irradiation embrittlement, i.e., rise in yield and flow stresses, and increase on DBTT. The main reason for these irradiation effects is that the irradiation-induced hardening increases the flow stress, and the plasticity localization weakens the overall hindering effect from ductile void growth on the cleavage nucleation and propagation, promoting the development of cleavage. Our probabilistic model takes into account the cleavage nucleation-propagation process and the influence of ductile void growth simultaneously, and it gives a sound explanation for the fundamental relation between the DBTT and mechanical properties of metallic materials.

Chemical-Reaction-Induced deformation of Body-Centered cubic iron in supercritical water leading to high risk of cleavage Fracture: A reactive Molecular dynamics study

Heterogeneous yielding mechanisms of body centered cubic iron for high resistance to chemical reaction-induced deterioration in supercritical water environments: A reactive molecular dynamics study

Reactive molecular dynamics study of the oxidation behavior of iron‐based alloy in supercritical water

Nanoscale ductile fracture and associated atomistic mechanisms in a body-centered cubic refractory metal

Reactive Molecular Dynamics Simulation Study on Atomic-Scale Adhesive Wear Mechanisms of Single Crystalline Body-Centered Cubic Iron

Atomistic Simulation of the Interaction between the Σ9[110](221) Shear-Coupled Grain Boundary Motion and the Cu-rich Precipitates in α-Iron

Atomic insights into the ductile–brittle competition of cracks under dissolution

Molecular Dynamics Simulation of Reinforcing Steel Corrosion when Subjected to Both Chloride Attack and Mechanical Loading

Molecular Dynamics Simulation of Brittle Fracture in Bcc Iron

The Effect of Point Defects Caused by Particle Bombardment on the Deformation Behaviours of Alpha-Iron: A Molecular Dynamics Simulation

Atomic insight into iron corrosion exposed to supercritical water environment with an improved Fe-H2O reactive force field

Atomic-scale Simulation of Α/γ-Iron Phase Boundary Affecting Crack Propagation Using Molecular Dynamics Method

Molecular Dynamics Simulation on Intergranular Crack Propagation Along ∑3 Tilt Grain Boundary in Bcc Iron

Molecular dynamics simulation of fracture in α-iron

Effects of Oxygen Concentration and Irradiation Defects on the Oxidation Corrosion of Body-Centered-cubic Iron Surfaces: A First-Principles Study

Atomistic simulation of crack cleavage and blunting in bcc-Fe

Mechanical degradations of Fe–C alloys induced by stress corrosion in supercritical CO2 environments: a study based on molecular dynamics simulation and machine learning

Softening Effects Due to Reorientations of Cu Precipitates in Α-Iron: Atomistic Simulations of Dislocations-Obstacles Interactions

Atomic Insights on Interaction Mechanism of Dislocation with Void/Impurity/Precipitates in BCC Iron

Probabilistic and Constitutive Models for Ductile-to-brittle Transition in Steels: A Competition Between Cleavage and Ductile Fracture

Corrosion Behavior of Oxide Dispersion Strengthened Ferritic Steels in Supercritical Water