Abstract:Titanium alloys are known for being difficult to machine. Within the groups of Ti alloys, the machinability is reduced when going from the α-alloys, to α + β, and finally to near-β or β-alloys. Uncoated cemented carbide is traditionally used for machining these alloys and finding a suitable coating to improve the performance is a challenge due to the high strength of Ti alloys and the high chemical reactivity of Ti with tool and coating materials at the temperatures achieved during cutting. The PVD applied Ti x Al 1-x N (x = 0.4–0.7) is generally recommended for machining Ti alloys and a top layer of NbN has shown promising performance in milling applications. This study systematically explores the wear mechanisms of either uncoated WC-12%Co or its Ti 0.45 Al 0.55 N-NbN coated version in the milling of Ti alloys ranging from near-α (Ti-6Al-2Sn-4Zr-2Mo), α + β (Ti-6Al-2Sn-4Zr-6Mo), and near-β (Ti-5Al-5Mo-5 V-3Cr) alloys. The wear evolution is explored by studying as-worn tools and their cross-section using SEM-XEDS and EBSD after having reached 10%, 30%, 50%, and 100% of the full tool life at a flank wear criterion VB = 200 μm. The coating is removed within seconds of engagement and fails by cracking within the bulk and PVD droplet defects can initiate such cracks. Diffusional dissolution of the coating may be active on a minor scale, but the rapid mechanical failure shows the need for a more robust coating formulation. Exposed cemented carbide is worn at varying intensities when machining the Ti alloys. The highest wear rate is achieved in milling α + β Ti-6246, followed by a moderate wear rate in near-β Ti-5553, and with a slower wear rate in milling near-α Ti-6242 which is explained varying intensities in oxidation wear, diffusional dissolution, and mechanical cracking. Diffusional loss of C gives rounder WC grains and remaining W at the interface is removed by the chip flow. Diffusional loss of Co gives reduced grain bonding and loss of the dampening effect that leads to fractures in WC grains. Specifically in milling α + β Ti-6246 and in minor scale in near-α Ti-6242, there is formation of CoWO 4 ceramic present several μm into the tool and its formation is facilitated by the oxidation of binder with resolved W. Fractures within the CoWO 4 explains the high wear rate. Cracks also propagate in binder regions initiated from weakened interface regions due to diffusional loss of C and Co.

Exploring the tribochemical wear and material transfer caused by Cu15Zn alloys on shearing tools

Mechanical properties and wear behaviors of Cu-doped zirconia-toughened alumina ceramics

Thermobarrier and antifriction properties of triboceramics on the surface of a cutting tool with (TiAlCrSiY)N/(TiAlCr)N coating during high-speed dry cutting

Adhesive wear mechanism of coated tools and its influence on cutting performance during machining of Zr-based bulk metallic glass

Wear mechanism of nanotwinned cBN tools in nano-cutting Ni-Cr-Fe alloy by molecular dynamics simulation

Dry Sliding Friction of Tool Steels and Their Comparison of Wear in Contact with ZrO2 and X46Cr13

Analysis of Tool Wear in GH4169 Material Milling Process

Mechanical and tribological properties of WC particles reinforced Cu-20Zn matrix composites

On the wear mechanisms of uncoated and coated carbide tools in milling titanium alloys

Analysis of tool wear of TiAlN coated tool, machined surface morphology and chip during titanium alloy milling

Understanding wear mechanisms of TiSiCN/Zr(C)N coatings at elevated temperatures

Comparative study of tool wear mechanisms in drilling ZrO2 ceramics using various tool types

Wear-resistant CrCoNi nanocrystalline film via friction-driven surface segregation

Microstructure and tribological behavior of a peak aged Cu–Cr–Zr alloy

Influence of self-lubricating elements (SrSO4, Mo, and CaF2) on machining performance of Al2O3-ZrO2 (Y2O3)-NiCr-Ag cutting tool over a wide cutting speed range

Tribological properties and wear resistance mechanism of WC-ZrO2-Al2O3 ceramics

Comparative analysis of the brazing mechanism and wear characteristics of brazed diamond abrasive with Zr-alloyed Cu-based filler metals

Abrasive Wear and Physical Properties of In-Situ Nano-TiCx Reinforced Cu–Cr–Zr Composites

Effect of in situ TiC reinforcement and applied load on the high-stress abrasive wear behaviour of zinc–aluminum alloy

Tribological and Electrochemical Corrosion Behaviors of Cu-based Powder Metallurgy Composites Reinforced by In-Situ WC with Different Morphology

Surface Fatigue Behavior of a WC/aC:H Thin-Film and the Tribochemical Impact of Zinc Dialkyldithiophosphate