Abrasive Wear Behavior of Batch Hot-Dip Galvanized Coatings

Thomas Pinger,Marco Brand,Sonja Grothe,Gabriela Marginean

DOI: https://doi.org/10.3390/ma17071547

IF: 3.4

2024-03-29

Materials

Abstract:In recent decades, batch hot-dip galvanized (HDG) steel has proven itself in practical applications due to the good corrosion resistance of its components. Despite the importance of the mechanical-load-bearing capacity of these coatings, the wear behavior has, so far, only been investigated very sporadically and not systematically, so a quantification of the wear behavior and statements on the mechanisms are vague. Therefore, two body wear tests with bonded abrasive grain were carried out. Varying the friction rolls, load, and total number of cycles, the wear behavior was investigated. The mass loss and the layer thickness reduction were measured at different intervals. After the test, the microstructure in the cross-section and the hardness according to Vickers (0.01 HV) were evaluated. The results showed that the wear behavior of HDG coatings against abrasive loads can be characterized with the selected test conditions. Initially, the applied load removed the soft η-phase. As the total number of cycles increases, the η- and ζ-phases deform plastically, resulting in a lower mass reduction compared to that expected from the measured layer thickness. The characteristic structure of a batch HDG coating with hard intermetallic Zn-Fe phases and an outer pure zinc phase has demonstrated effective resistance to abrasion.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: **There is still a lack of systematic research on the behavior of batch hot - dip galvanizing (HDG) coatings under mechanical wear, especially under abrasive wear conditions, resulting in insufficient understanding of their wear mechanisms and quantitative characteristics.**

Specifically, although batch hot - dip galvanized steel shows good corrosion resistance in practical applications, its wear resistance under mechanical loads has not been fully studied. Therefore, this paper systematically studied the wear behavior of batch hot - dip galvanized coatings under different friction wheels, loads and cycle numbers through two - body abrasive wear tests. The research content includes measuring mass loss and coating thickness reduction, and evaluating microstructure and Vickers hardness.

### Key problem summary:
1. **Lack of systematic research**: At present, there are few and not systematic enough studies on the wear behavior of batch hot - dip galvanized coatings.
2. **Unclear wear mechanism**: The specific wear mechanisms of these coatings under abrasive wear conditions are limitedly understood.
3. **Vague quantitative characteristics**: The specific wear characteristics and quantitative data of these coatings are rather vague.

Through this study, the author hopes to fill the knowledge gap in this field and provide more accurate scientific basis for industrial applications.