Battery waste-derived magnetic Fe–Mn–Zn/C composites as an electro-Fenton-like catalyst for the degradation of sodium dodecyl sulfate surfactant

Azhan Ahmad,Monali Priyadarshini,Makarand M. Ghangrekar,Rao Y. Surampalli

DOI: https://doi.org/10.2166/wst.2024.033

IF: 2.43

2024-02-07

Water Science & Technology

Abstract:A batch-scale electro-Fenton (EF) process was performed using graphite anode and waste battery-based Fe–Mn–Zn/C electrocatalyst coated on low-cost graphite felt cathode. The effectiveness of the EF's performance was evident with around 83.9 ± 4.1% removal of 20 mg/L of sodium-dodecyl sulfate surfactant (SDS) at an optimum current density (CD) of 5.0 mA/cm2, Na2SO4 of 0.05 M, initial pH of 7.2, and electrolysis time of 180 min. Moreover, nearly 1.78-fold more removal of SDS was achieved in EF than in the electro-oxidation process operated without any catalyst. The operating cost of 0.35 $ of per m3 per order was needed to treat SDS wastewater. The remediation of SDS follows pseudo-first-order kinetics with a rate constant of 0.0095 min−1. Additionally, 90.3 ± 2.1% of SDS and 57 ± 2.6% of total organic carbon (TOC) removal was attained during 240 min of treatment time in secondary treated real wastewater; hence, additional 60 min of treatment time is required for effectively treating real wastewater than synthetic wastewater. The pathway of SDS degradation suggests the formation of lauric acid as an intermediate by-product, which is an environmentally affordable product. Thus, EF is effective with battery waste-derived magnetic catalyst for treating wastewater containing SDS, which can lead to achieving sustainable environmental goals.

environmental sciences,engineering, environmental,water resources