Vasilios Karanikolas,Takuya Iwasaki,Joel Henzie,Naoki Ikeda,Yusuke Yamauchi,Yutaka Wakayama,Takashi Kuroda,Kenji Watanabe,Takashi Taniguchi

DOI: https://doi.org/10.48550/arXiv.2211.09339

2022-11-17

Abstract:High-quality emission centers in two-dimensional materials are promising components for future photonic and optoelectronic applications. Carbon-enriched hexagonal boron nitride (hBN:C) layers host atom-like color-center (CC) defects with strong and robust photoemission up to room temperature. Placing the hBN:C layers on top of Ag triangle nanoparticles (NPs) accelerate the decay of the CC defects down to 46 ps from their reference bulk value of 350 ps. The ultrafast decay is achieved due to the efficient excitation of the plasmon modes of the Ag NPs by the near field of the CCs. Simulations of the CCs/Ag NP interaction present that higher Purcell values are expected, although the measured decay of the CCs is limited by the instrument response. The influence of the NP thickness to the Purcell factor of the CCs is analyzed. The ultrafast operation of the CCs in hBN:C layers paves the way for their use in demanding applications, such as single-photon emitters and quantum devices.

Optics,Materials Science,Quantum Physics

What problem does this paper attempt to address?

The problem this paper attempts to solve is: how to achieve ultrafast operation by accelerating the luminescence decay process of color center (CC) defects through placing a carbon-enriched hexagonal boron nitride (hBN:C) layer on silver triangular nanoparticles (Ag NPs). Specifically, the researchers aim to reduce the decay time of CC defects from 350 picoseconds to 46 picoseconds through this structural design, thereby enhancing the potential applications of these materials in photonics and quantum technologies.

### Background
- **High-quality luminescent centers**: High-quality luminescent centers in 2D materials are crucial components for future photonic and optoelectronic applications.
- **Carbon-enriched hexagonal boron nitride (hBN:C)**: This material contains atomic-level color center (CC) defects with robust room-temperature light emission properties.
- **Surface plasmon resonance (Plasmon)**: Silver nanoparticles (Ag NPs) can support surface plasmon modes, which can significantly accelerate the luminescence decay of CC when interacting with the near field of the CC in the hBN:C layer.

### Objectives
- **Accelerate CC luminescence decay**: By placing the hBN:C layer on Ag NPs, utilize the surface plasmon modes of Ag NPs to accelerate the luminescence decay process of CC.
- **Achieve ultrafast operation**: Reduce the decay time of CC from 350 picoseconds to 46 picoseconds to achieve ultrafast operation.
- **Enhance quantum application potential**: Ultrafast operation can reduce dephasing effects, which is crucial for applications in quantum computing, communication, and sensing.

### Methods
- **Sample preparation**: First, transfer the hBN:C layer onto a SiO2/Si substrate, then place it on Ag NPs using a dry transfer technique.
- **Experimental measurement**: Use a homemade confocal microscope system to measure the light emission signal and extract the decay time constant through single-exponential fitting.
- **Theoretical simulation**: Study the near-field interaction between CC and Ag NPs through numerical simulations and calculate the Purcell factor.

### Results
- **Experimental results**: After placing the hBN:C layer on Ag NPs, the decay time of CC was reduced from 350 picoseconds to 46 picoseconds, with a Purcell factor of approximately 8.
- **Theoretical prediction**: Numerical simulations indicate that higher Purcell factor values are possible, especially when CC is close to the edge of Ag NPs.

### Conclusion
By placing the hBN:C layer on Ag NPs, the luminescence decay process of CC can be significantly accelerated, achieving ultrafast operation. This result opens up new possibilities for developing compact quantum applications.