Zwitterionic interface engineering enables ultrathin composite membrane for high-rate vanadium flow battery

Denghua Zhang,Xihao Zhang,Chao Luan,Biao Tang,Zhongyu Zhang,Nianwen Pu,Kaiyue Zhang,Jianguo Liu,Chuanwei Yan
DOI: https://doi.org/10.1016/j.ensm.2022.04.033
IF: 20.4
2022-08-01
Energy Storage Materials
Abstract:Thin membranes with high conductivity are of great importance for high power density vanadium flow batteries (VFBs), however, the trade-off between conductivity and ion selectivity limits their further development. Herein, an ultrathin composite membrane (∼10 μm) enabled by a zwitterionic interface between conductive polybenzimidazole (PBI) and porous polyethylene (PE) substrate is proposed to break the trade-off, and greatly enhance the power density of a VFB. The zwitterionic interface is engineered by the covalent reaction between polydopamine and zwitterionic sulfonated 3-dimethylaminopropylamine (DMAPAPS). The as-fabricated composite membrane features excellent mechanical properties and high dimensional stability. Furthermore, the zwitterionic interface facilitates proton transportation while blocking vanadium-ion permeation. More importantly, the ion selectivity of the ultrathin membrane is nearly three times higher than the pure PBI membrane (i.e., 2.71 × 104 vs. 1.09 × 104 S min cm−3). As a result, a VFB assembled with the ultrathin membrane demonstrates a superior energy efficiency of 78.7% at 300 mA cm−2, and achieves an excellent cycle stability over 500 cycles at 300 mA cm−2. Therefore, the engineering of zwitterionic interface provides a promising strategy in the development of ultrathin composite membrane for high power density VFBs.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology
What problem does this paper attempt to address?