Abstract:Coupling TiO2 with various elements could enhance its photocatalytic activity. In this study, an innovative ultrasound-assisted sol–gel method was used to synthesize TiO2/Ag(x%) by varying Ag–support mass (x = 9.3, 17.1, and 23.6%), followed by calcination at 450 °C for 30 min. The aim was to demonstrate that Ag compositing improves photoactivity under visible light (>400 nm). The synthesized photocatalysts were assessed for their effectiveness in the degradation and mineralization of Methylene Blue (MB) and Acid Orange 7 (AO7) using visible lamps emitting in the range of 400–800 nm. Characterization of the prepared photocatalysts was performed by using Raman spectroscopy, SEM/EDS, pHpzc, and UV–visible spectroscopy. Raman spectroscopy confirmed the predominance of the anatase phase in all the photocatalysts. The photodegradation efficiencies of the selected dyes, MB and AO7, reached 99% (pH 6) and 95% (pH 3) after 180 min of irradiation, respectively. The best performance for the degradation of the two dyes was observed with TiO2/Ag9.3%, showing optimal kinetics at this doping concentration. The improved photoactivity of the TiO2/Ag composite is due to a decrease in the recombination rate of electron/hole (e−/h+) and a decrease in the band gap from 3.13 to 2.49 eV. The mineralization rate of both dyes under visible light is about 9.3%, indicating the presence of refractory by-products that resist complete degradation. Under UVA irradiation, complete mineralization is obtained. This study confirms the potential of TiO2/Ag composite as a high-performance and cost-effective photocatalyst for solar environmental remediation, highlighting the role of silver in extending light absorption into the visible region and improving charge separation.

One-step synthesis of Ag3VO4/diatomite composite material for efficient degradation of organic dyes under visible light

Synthesis and Photocatalytic Mechanism Study of Visible Light-Driven Z-type Ag/AgBr/Bi2MoO6 Composite Materials for Efficient Degradation of Organic Dyes

Synthesis of Nano-Tio2/diatomite Composite and Its Photocatalytic Degradation of Gaseous Formaldehyde

Ag3PO4/graphene-oxide composite with remarkably enhanced visible-light-driven photocatalytic activity toward dyes in water.

Graphene Quantum Dots Modified Ag3PO4 for Facile Synthesis and the Enhanced Photocatalytic Performance

Photocatalytic Degradation of Organic Dyes by a High Efficient TiO<sub>2</sub>-Based Catalysts Under Solar Light Irradiation

Ag3VO4/AgI Composites for Photocatalytic Degradation of Dyes and Tetracycline Hydrochloride under Visible Light

Synthesis of Natural Porous Minerals Supported Tio2 Nanoparticles and Their Photocatalytic Performance Towards Rhodamine B Degradation

A Comparative Study of Different Diatomite-Supported Tio2 Composites and Their Photocatalytic Performance for Dye Degradation

Ag-Ag3VO4/AgIO3 Composites with Enhanced Visible-Light-driven Catalytic Activity.

Preparation Ag3PO4/AgVO3/Ag4V2O7 Composites for Enhancing Visible Light Photocatalytic Activity of Ag3PO4

A Novel Step-Scheme BiVO4/Ag3VO4 Photocatalyst for Enhanced Photocatalytic Degradation Activity under Visible Light Irradiation

Efficient degradation of atrazine residues in wastewater by persulfate assisted Ag3VO4/Bi2MoO6/diatomite under visible light

Facile synthesis of Ag3PO4 modified with GQDs composites with enhanced visible-light photocatalytic activity

Facile preparation of Yb3+/Tm3+ co-doped Ti3C2/Ag/Ag3VO4 composite with an efficient charge separation for boosting visible-light photocatalytic activity

Construction of Z-scheme Ag3PO4/Bi2WO6 Composite with Excellent Visible-Light Photodegradation Activity for Removal of Organic Contaminants

Efficient degradation of dye pollutants on nanoporous polyoxotungstate–anatase composite under visible-light irradiation

Fabrication of Ag/WO3/g-C3N4 composites for the photocatalytic degradation of harmful dyes

Synthesis of Nanosized Ag3vo4 Particles and Their Photocatalytic Activity for Degradation of Rhodamine B under Visible Light

Enhanced Visible-Light Photocatalysis Activity of TiO2/Ag Nanocomposites Prepared by the Ultrasound-Assisted Sol–Gel Method: Characterization and Degradation–Mineralization of Cationic and Anionic Dyes

Synthesis and Characterization of G-C3n4/ag3vo4 Composites with Significantly Enhanced Visible-Light Photocatalytic Activity for Triphenylmethane Dye Degradation