Self-Healing Activation by Conventional Resistive Heating through the Addition of Carbon Nanotubes in Epoxy Systems Based on Covalent Adaptable Networks

Javier Gómez-Sánchez,Xoan Xosé Fernández Sánchez-Romate,Alberto Jiménez-Suárez,Silvia G. Prolongo,Javier Gómez-Sánchez,Xoan Xosé Fernández Sánchez-Romate,Alberto Jiménez-Suárez

DOI: https://doi.org/10.1021/acsapm.3c01022

2024-01-10

ACS Applied Polymer Materials

Abstract:A study of the self-healing capabilities of 2-aminophenyl disulfide (AFD)/epoxy systems is carried out. It has been observed that an excess of AFD promotes an increase of both the storage modulus and the glass transition temperature (T g) due to an increase of the cross-link density. Concerning the self-healing properties, every AFD/epoxy system shows very good healing efficiencies (above 90%) with no prevalent differences among the different stoichiometries. Furthermore, CNT addition induces an increase of the storage modulus when there is no excess of AFD, but no significant effect is observed on the T g. In addition, the incorporation of these nanoparticles allows thermal activation by the Joule effect. The results of self-healing tests under convective and resistive heating show similar healing efficiencies (all above 94%). Here, the thermal activation by Joule’s heating presents a lower power consumption and allows localized repair, which is very promising for this type of application.

polymer science,materials science, multidisciplinary

What problem does this paper attempt to address?

The paper primarily explores the self-healing performance of a bis(dithiocarbamate) (AFD)/epoxy resin system by adding carbon nanotubes (CNTs) and investigates the method of activating self-healing performance through traditional resistive heating.

Research Background:
- Epoxy resins are widely used in high-performance structural applications due to their high cross-link density, low shrinkage, and high strength, but their brittle behavior leads to performance degradation during service.
- To address the above issues, researchers consider incorporating dynamic networks into thermosetting polymers to impart self-healing functions, thereby repairing damage and cracks, restoring the material's original performance, and extending its service life.
- The self-healing mechanism studied in this paper is based on disulfide bond exchange reactions, which can be activated by photolysis, heating, or oxidation.

Specific research content includes:
1. **Study of self-healing capability**: The self-healing efficiency of different ratios of AFD/epoxy resin systems (including stoichiometric and excess AFD cases) was studied and tested under convective heating conditions in a traditional oven. The results showed that the self-healing efficiency of all systems was above 90%.
2. **Impact of carbon nanotubes**: By adding carbon nanotubes (CNTs), self-healing can be achieved under resistive heating. The impact of CNT addition on thermomechanical properties was studied, and the variation in self-healing efficiency with different CNT contents was evaluated.
3. **Comparison of self-healing efficiency**: The self-healing efficiency under convective heating and resistive heating was compared, and it was found that the self-healing efficiency was similar under both heating methods (both above 94%), but resistive heating had the advantages of lower energy consumption and localized heating.

Conclusion:
- By increasing the amount of AFD, the storage modulus and glass transition temperature (Tg) of the material can be improved due to the increase in cross-link density.
- Without compromising self-healing efficiency, self-healing activation under resistive heating was achieved by adding carbon nanotubes, which has lower energy consumption and allows for localized repair.
- This study provides a new approach for developing high-performance self-healing composites.