3D Hierarchical NiCo 2 S 4 Nanoparticles/Carbon Nanotube Sponge Cathode for Highly Compressible Asymmetric Supercapacitors

Xiaoming Yang,Xuexia He,Qi Li,Jie Sun,Zhibin Lei,Zong-Huai Liu
DOI: https://doi.org/10.1021/acs.energyfuels.0c03745
2021-01-29
Abstract:By employing a carbon nanotube (CNT) sponge with a 3D porous network as a compressible substrate and NiCo<sub>2</sub>S<sub>4</sub> nanoparticles as active materials, a NiCo<sub>2</sub>S<sub>4</sub>/CNT sponge electrode with high compression characteristics and prominent capacitance is fabricated by a solvothermal method. NiCo<sub>2</sub>S<sub>4</sub> nanoparticles with size ranging from 20 to 25 nm are evenly anchored on the network of a CNT sponge, making it show excellent compression performance and large specific capacitance of 1110 F g<sup>–1</sup>. Meanwhile, a Fe<sub>2</sub>O<sub>3</sub>/CNT sponge as an anode with a specific capacitance of 330 F g<sup>–1</sup> for a widening voltage window is also fabricated by hydrothermal reaction technology. A NiCo<sub>2</sub>S<sub>4</sub>/CNT//Fe<sub>2</sub>O<sub>3</sub>/CNT asymmetric supercapacitor with high compression is assembled using a NiCo<sub>2</sub>S<sub>4</sub>/CNT sponge and an Fe<sub>2</sub>O<sub>3</sub>/CNT sponge as the cathode and anode electrode, respectively, and its potential window can reach up to 1.7 V. The assembled device not only delivers a high specific capacitance of 117 F g<sup>–1</sup> at 1 A g<sup>–1</sup>, but also shows excellent compression and flexibility. Moreover, it exhibits a superior energy density of 41.6 W h kg<sup>–1</sup> and excellent long-run cyclic stability that retains about 82% of the initial capacitance after 5000 cycles under about 80% strain. The NiCo<sub>2</sub>S<sub>4</sub>/CNT//Fe<sub>2</sub>O<sub>3</sub>/CNT asymmetric supercapacitor may offer a feasible approach for assembling compressible energy devices on account of its remarkable compression property, superior specific capacitance, and distinguished Coulombic efficiency.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.energyfuels.0c03745?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.energyfuels.0c03745</a>.Experimental section; XRD patterns of NiCo<sub>2</sub>S<sub>4</sub> nanoparticles and NiCo<sub>2</sub>S<sub>4</sub>/CNT-33 sponge; SEM images of NiCo<sub>2</sub>S<sub>4</sub>/CNT sponge electrodes obtained by solvothermal treating in different concentrations of Ni(NO<sub>3</sub>)<sub>2</sub>·6H<sub>2</sub>O·6H<sub>2</sub>O with a molar ratio of Co:Ni = 2 for 10 h at 180 °C: (a) pure CNT, (b) NiCo<sub>2</sub>S<sub>4</sub>/CNT-8.3, (c) NiCo<sub>2</sub>S<sub>4</sub>/CNT-17, (d) NiCo<sub>2</sub>S<sub>4</sub>/CNT-33, (e) NiCo<sub>2</sub>S<sub>4</sub>/CNT-50, and (f) NiCo<sub>2</sub>S<sub>4</sub>/CNT-67; electrochemical properties of NiCo<sub>2</sub>S<sub>4</sub>/CNT sponge electrodes obtained by solvothermal treating in different concentrations with a molar ratio of Co:Ni = 2 for 10 h at 180 °C in 3 M KOH: (a) CV curves, (b) GCD curves, (c) Nyquist plot over the frequency range of 100 kHz to 0.1 Hz, and (d) specific capacitance at different current densities; NiCo<sub>2</sub>S<sub>4</sub>/CNT-33 sponge electrode corresponding <i>b</i>-value found by using the peak current relationship to the scan rate; specific capacitance of the NiCo<sub>2</sub>S<sub>4</sub>/CNT-33 sponge at each evaluated current density for different set strains; and compressive stress–strain curves of the asymmetric supercapacitor at different strains (<a class="ext-link" href="/doi/suppl/10.1021/acs.energyfuels.0c03745/suppl_file/ef0c03745_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
energy & fuels,engineering, chemical
What problem does this paper attempt to address?