Thermal motion of skyrmion arrays in granular films

Yifan Zhou,Rhodri Mansell,Tapio Ala-Nissila,Sebastiaan van Dijken

DOI: https://doi.org/10.1103/PhysRevB.104.144417

2021-03-18

Abstract:Magnetic skyrmions are topologically-distinct swirls of magnetic moments which display particle-like behaviour, including the ability to undergo thermally-driven diffusion. In this paper we study the thermally activated motion of arrays of skyrmions using temperature dependent micromagnetic simulations where the skyrmions form spontaneously. In particular, we study the interaction of skyrmions with grain boundaries, which are a typical feature of sputtered ultrathin films used in experimental devices. We find the interactions lead to two distinct regimes. For longer lag times the grains lead to a reduction in the diffusion coefficient, which is strongest for grain sizes similar to the skyrmion diameter. At shorter lag times the presence of grains enhances the effective diffusion coefficient due to the gyrotropic motion of the skyrmions induced by their interactions with grain boundaries. For grain sizes significantly larger than the skyrmion diameter clustering of the skyrmions occurs in grains with lower magnetic anisotropy.

Mesoscale and Nanoscale Physics,Materials Science

What problem does this paper attempt to address?

This paper aims to study the thermal motion characteristics of magnetic skyrmions in polycrystalline thin films, especially to explore the influence of the interaction between skyrmions and grain boundaries on their diffusion coefficients. Specifically, the article attempts to solve the following problems:

1. **Understanding the diffusion behavior of skyrmions in polycrystalline thin films**:
- The influence of grain boundaries on the skyrmion diffusion coefficient at different time scales.
- The motion mechanism of skyrmions at the grain boundaries, including their drift along the boundaries and jumps across the boundaries.

2. **Revealing the influence of grain size and magnetic anisotropy changes on skyrmion diffusion**:
- How the grain size affects the skyrmion diffusion coefficient, especially the differences at short and long lag times.
- How the change of magnetic anisotropy affects the skyrmion diffusion behavior, especially its performance at different grain sizes.

3. **Exploring the aggregation phenomenon of skyrmions in polycrystalline thin films**:
- Skyrmions tend to aggregate in grains with low magnetic anisotropy. How does this phenomenon perform at different grain sizes?
- How does the existence of grains change the spatial distribution and density of skyrmions?

### Main findings

- **Long lag time (>5 ns)**: For larger grains, the grain boundaries will prevent skyrmions from entering adjacent grains but allow them to diffuse inside the grains. As the grain size increases, the diffusion coefficient increases. When approaching the grain boundaries, skyrmions will be subject to a force away from the boundaries (caused by the dissipation term) and a force to move along the boundaries (caused by the precession term), which makes it difficult for skyrmions to cross large - sized grain boundaries.

- **Short lag time (<0.1 ns)**: Grain boundaries will hinder the thermally - induced precession motion, thereby enhancing the diffusivity of skyrmions. Especially for grain sizes from 1 nm to 5 nm, the skyrmion diffusion coefficient increases significantly.

- **When the grain size is close to the skyrmion diameter**: Skyrmions almost continuously interact with the grain boundaries and are effectively pinned by a single low - anisotropy grain, resulting in a diffusion coefficient close to zero at long lag times.

- **When the grain size is much smaller than the skyrmion diameter**: Skyrmions are affected by the forces of multiple grain boundaries. Although the pinning force is smaller than that of medium - sized grains, the diffusion coefficient may still be close to zero in the case of large anisotropy changes.

### Formula summary

- **Thiele equation**:
\[
M_s \gamma^{-1} G \times \dot{C} + M_s \gamma^{-1} \alpha D \cdot \dot{C} = F_T + F_I + F_G
\]
where,
- \( M_s \) is the saturation magnetization,
- \( \gamma \) is the gyromagnetic ratio,
- \( \alpha \) is the magnetic damping constant,
- \( G \) is the precession coupling vector,
- \( D \) is the dissipation force tensor,
- \( F_T \) is the thermal force,
- \( F_I \) is the interaction force between skyrmions,
- \( F_G \) is the effective force caused by the grain boundaries.

- **Diffusion coefficient**:
\[
D = \frac{k_B T \alpha D}{G^2+(\alpha D)^2}
\]
where,
- \( k_B \) is the Boltzmann constant,
- \( T \) is the temperature.

These research results are helpful for experimental design, especially for using the thermal motion of skyrmions to create logic devices, and provide a theoretical basis for controlling these devices through grain engineering.