Abstract:Bolland and Gee's basic autoxidation scheme (BAS) for lipids and rubbers has long been accepted as a general scheme for the autoxidation of all polymers. This scheme describes a chain process of initiation, propagation, and termination to describe the degradation of polymers in the presence of O2. Central to this scheme is the conjecture that propagation of damage to the next polymer chain occurs via hydrogen atom transfer with a peroxyl radical. However, this reaction is strongly thermodynamically disfavored for all but unsaturated polymers, where the product allylic radical is resonance-stabilized. Paradoxically, there is no denying that the autocatalytic degradation and oxidation of saturated polymers still occurs. Critical analysis of the literature, described herein, has begun to unravel this mystery. One possibility is that the BAS still holds for saturated polymers but only at unsaturated defect sites, where H transfer is thermodynamically favorable. Another is that peroxyl termination rather than H transfer is dominant. If this were the case, tertiary peroxyl radicals (formed at quaternary centers or quaternary branching defects) may terminate to form alkoxy radicals, which can much more readily undergo chain transfer. This process would lead to the creation of hydroxy groups on the degraded polymer. On the other hand, primary and secondary peroxyl radicals would terminate to form nonradical products and halt further degradation. As a result, under this scenario the degree of branching and substitution would have a major effect on polymer stability. Herein we survey studies of polymer degradation products and of the effect of polymer structure on stability and show that indeed peroxyl termination is competitive with peroxyl transfer and possibly dominant under some conditions. It is also feasible that oxygen may not be the only reactive atmospheric species involved in catalyzing polymer degradation. Herein we outline plausible mechanisms involving ozone, hydroperoxyl radical, and hydroxyl radical that have all been suggested in the literature and can account for the experimentally observed formation of hydroperoxides without invoking peroxyl transfer. We also show that oxygen itself has even been reported to slow the degradation of poly(methyl methacrylate)s, which might be expected if peroxyl radicals are unreactive toward hydrogen transfer. Discrepancies between the rate of oxidation and the rate of degradation have been observed for polyolefins and also support the counterintuitive notion that oxygen stabilizes these polymers against degradation. We show that together these studies support alternative mechanisms for polymer degradation. A thorough assessment of kinetic studies reported in the literature indicates that they are limited by their propensity to use models based on the BAS, disregarding the chemical differences intrinsic to each class of polymer. Thus, we propose that further work must be done to fully grasp the complex mechanism of polymer degradation under ambient conditions. Nonetheless, our analysis of the literature points to measures that can be used to enhance or prevent polymer degradation and indicates that we should focus beyond just the role of oxygen toward the specific chemical nature and environment of the polymer at hand.

Atomic scale mechanisms controlling the oxidation of polyethylene: a first principles study

Mechanistic Understanding of Efficient Polyethylene Hydrocracking over Two-Dimensional Platinum-Anchored Tungsten Trioxide.

Physics and Chemistry-Based Constitutive Modeling of Photo-Oxidative Aging in Semi-Crystalline Polymers

A Quantum Chemical and Molecular Dynamics Simulation Study on Photo-Oxidative Aging of Polyethylene: Mechanism and Differences between Crystalline and Amorphous Phases

Thermo‐oxidative degradation of additive free polyethylene. Part I. Analysis of chemical modifications at molecular and macromolecular scales

Quantum Mechanical Investigation of the Oxidative Cleavage of the C–C Backbone Bonds in Polyethylene Model Molecules

The Fate of the Peroxyl Radical in Autoxidation: How Does Polymer Degradation Really Occur?

Reactions of a prototypical phenolic antioxidant with radicals in polyethylene: insights from density functional theory

Atomic insights into the thermal degradation of polyethylene terephthalate combining STA-FTIR and DFT methods

Effect of Structure and Morphology on Photo-Oxidation Degradation of Polyethylene

Theoretical determination of a model molecule for the catalytic upcycling of polyolefins

Quantum Simulations of Radiation Damage in a Molecular Polyethylene Analog

How Small Molecules Affect the Thermo-Oxidative Aging Mechanism of Polypropylene: A Reactive Molecular Dynamics Study

A reactive molecular dynamics simulation of the atomic oxygen impact on poly(p-phenylene-terephthalamide)

Spin Trapping Analysis of Radical Intermediates on the Thermo-Oxidative Degradation of Polypropylene

The effects of atomic oxygen and ion irradiation degradation on multi-polymers: A combined ground-based exposure and ReaxFF-MD simulation

Study on the atomic scale of thermal and thermo-oxidative degradation of polylactic acid via reactive molecular dynamics simulation

Micromechanically informed reaction-induced damage and fracture in polymers due to oxidation

A DFT mechanistic study on the N‐acyloxyamine‐initiated controlled degradation of polypropylene

Effects of Crystallinity and Branched Chain on Thermal Degradation of Polyethylene: A SCC-DFTB Molecular Dynamics Study

Physics-based Constitutive Modeling of Photo-oxidative Aging in Semi-Crystalline Polymers based on Chemical Characterization Techniques