Structural Phase Transition and Interlayer Coupling in Few-Layer 1T' and Td MoTe2

Yeryun Cheon,Soo Yeon Lim,Kangwon Kim,Hyeonsik Cheong

DOI: https://doi.org/10.1021/acsnano.0c09162

2021-01-22

Abstract:We performed polarized Raman spectroscopy on mechanically exfoliated few-layer MoTe2 samples and observed both 1T' and Td phases at room temperature. Few-layer 1T' and Td MoTe2 exhibited a significant difference especially in interlayer vibration modes, from which the interlayer coupling strengths were extracted using the linear chain model: strong in-plane anisotropy was observed in both phases. Furthermore, temperature-dependent Raman measurements revealed a peculiar phase transition behavior in few-layer 1T' MoTe2. In contrast to bulk 1T' MoTe2 crystals where the phase transition to the Td phase occurs at ~250 K, the temperature-driven phase transition to the Td phase is increasingly suppressed as the thickness is reduced, and the transition and the critical temperature varied dramatically from sample to sample even for the same thickness. Raman spectra of intermediate phases that correspond to neither 1T' nor Td phase with different interlayer vibration modes were observed, which suggests that several metastable phases exist with similar total energies.

Mesoscale and Nanoscale Physics

What problem does this paper attempt to address?

The problems that this paper attempts to solve mainly focus on the following aspects:

1. **Stability and transition mechanisms of different phase states**:
- The paper explores the stability of two different phase states (1T′ and Td) existing in MoTe₂ materials at room temperature and their mutual transition mechanisms. In particular, in few - layer samples, the coexistence of these two phase states has aroused the interest of researchers.
- Through polarized Raman spectroscopy, researchers have observed the coexistence of 1T′ and Td phases at room temperature and found significant differences between them, especially in the interlayer vibration modes.

2. **Temperature - driven phase - change behavior**:
- The research found that in bulk 1T′ MoTe₂ crystals, the phase change occurs when the 1T′ phase transforms into the Td phase at about 250 K. However, for multi - layer samples, as the thickness decreases, this temperature - driven phase change is gradually suppressed, and the critical temperature differences among different samples with the same thickness are significant.
- Temperature - dependent Raman spectroscopy measurements revealed that multi - layer 1T′ MoTe₂ samples exhibit different phase - change behaviors during the cooling process: some samples have obvious phase changes, while others do not occur or only show intermediate phase states.

3. **Interlayer coupling strength and anisotropy**:
- Through the linear chain model, researchers extracted the interlayer coupling strength. The results show that the 1T′ and Td phases exhibit strong in - plane anisotropy, which is similar to the situation in black phosphorus.
- The change in interlayer coupling strength not only affects the phase - change behavior but also results in a very small energy difference between different phase states, thus explaining why the coexistence of two phase states can be observed in multi - layer samples.

4. **Existence of intermediate phase states**:
- The research also found several intermediate phase states that are neither 1T′ nor Td phases. These phase states have different interlayer vibration modes, indicating the existence of multiple metastable phases.
- The existence of these intermediate phase states further complicates the phase - change process. In particular, during temperature changes, some samples show incomplete phase changes or mixed phase states.

In summary, this paper aims to deeply understand the phase - change behavior, interlayer coupling characteristics of MoTe₂ materials in multi - layer structures, and the influence of temperature on their stability, providing important theoretical and experimental bases for future material design and applications.