Abstract:In this paper, the effect of thermomechanical treatment process on the hardening behavior, grain microstructure, precipitated phase, and tensile mechanical properties of the new high-strength and high-ductility Al-10.0Zn-3.0Mg-2.8Cu alloy was studied, and the optimal thermomechanical treatment process was established. The strengthening and toughening mechanisms were revealed, which provided technical and theoretical guidance for the engineering application of this kind of high strength-ductility aluminum alloy. Al-10.0Zn-3.0Mg-2.8Cu alloy cylindrical parts with external longitudinal reinforcement were prepared by a composite extrusion deformation process (reciprocal upsetting + counter-extrusion) with a true strain up to 2.56, and the organizational evolution of the alloys during the extrusion deformation process and the influence of pre-stretching treatments on the subsequent aging precipitation behaviors and mechanical properties were investigated. The results show that firstly, the large plastic deformation promotes the fragmentation of coarse insoluble phases and the occurrence of dynamic recrystallization, which results in the elongation of the grains along the extrusion direction, and the volume fraction of recrystallization reaches 42.4%. Secondly, the kinetic study showed that the decrease in the activation energy of precipitation increased the nucleation sites, which further promoted the diffuse distribution of the second phase in the alloy and a higher number of nucleation sites, while limiting the coarsening of the precipitated phase. When the amount of pre-deformation was increased from 0% to 2%, the size of the matrix precipitated phase decreased from 5.11 μm to 4.1 μm, and when the amount of pre-deformation was increased from 2% to 7%, the coarsening of the matrix precipitated phase took place, and the size of the phase increased from 4.1 μm to 7.24 μm. The finalized heat treatment process for the deformation of the aluminum alloy tailframe was as follows: solution (475 °C/3 h) + 2% pre-stretching + aging (120 °C/24 h), at which the comprehensive performance of the alloy was optimized, with a tensile strength of 634.2 MPa, a yield strength of 571.0 MPa, and an elongation of 15.2%. The alloy was strengthened by both precipitation strengthening and dislocation strengthening. After 2% pre-stretching, the fracture surface starts to be dominated by dense tough nest structure, and most of them are small tough nests, and small and dense tough nests are the main reason for the increase in alloy toughness after 2% pre-stretching deformation.

Study of strengthening mechanisms in Al-Cu and Al-Cu-Mg systems subjected to plastic deformation and T6 treatment

Effect on Microstructure and Hardness of Reinforcement in Al–Cu with Al4C3 Nanocomposites

Study on strengthening and toughening mechanisms of cu/Al composites dominated by interface layer

Evolution of Properties of High-Strength and High-Mg-Content CuMg Alloys After Being Subjected to Single Operation 50% Deformation in Hot and Cold Upsetting Tests

The Microstructure, and Mechanical and Corrosion Properties of As-Cast and As-Extruded Mg-2%Zn-x%Cu Alloys After Solution and Aging Heat Treatments

Tailoring the microstructure, mechanical properties, and electrical conductivity of Cu–0.7Mg alloy via Ca addition, heat treatment, and severe plastic deformation

Improving the stretch formability of a heat-treatable magnesium–aluminum–calcium–manganese alloy by copper addition at the parts-per-million-level

A multidisciplinary approach to study precipitation kinetics and hardening in an Al-4Cu (wt. %) alloy

Acquiring Mg-Ag microalloying TiB 2 /Al-4.5Cu composite simultaneously with ultrahigh strength and ductility via optimized salt-metal reaction and multistage heat treatment

Deformation mechanisms and mechanical properties of the high-strength and ductile Al-Zn-Mg-Cu alloys processed by repetitive continuous extrusion forming process with different heat treatments

Utilizing integrated neutron diffraction and elastoplastic self-consistent crystal plasticity model to quantitatively assess the strengthening mechanism in Al-12.5Ce and Al-12.5Ce-0.4Mg alloys

Effects of Copper Content and Thermo-Mechanical Treatment on Microstructure and Mechanical Properties of AlMgSi(Cu) Alloys

Formation of high strength Mg–Cu–Zn–Y alloys

Detailed investigation on microstructure and strengthening contribution of Al- x Cu-1.3Li-X alloy sheets

Enhancing the mechanical properties of Mg-Zn-Al-Cu-Mn alloy via MgCO3 inoculation treatment: Experimental studies and first-principles calculations

Influence of Mg Doping on the Structure and Mechanical Properties of Al2Cu Precipitated Phase by First-Principles Calculations

Ultra-high strength Al-Zn-Mg-Cu alloys with high zinc content prepared via powder hot extrusion

The microstructures and mechanical properties of a highly alloyed Al-Zn-Mg-Cu alloy: The role of Cu concentration

Study on the Aging Precipitation Behavior and Kinetics of Al-10.0Zn-3.0Mg-2.8Cu Alloy by Pre-Deformation Treatment

Hot Deformation Behavior and Microstructure Evolution of High-Strength Al-Zn-Mg-Cu Alloy

Evolution of the microstructure and properties of a Cu–Cr-(Mg) Alloy upon thermomechanical treatment