Abstract:The successful synthesis of PtMn3N intermetallic compounds exhibits superior oxygen reduction performance. The introduction of Mn elements to the Pt lattice is beneficial to producing appropriate compressive strain to weaken the binding energy of oxygen species and the strong metal‐N interactions are conducive to alleviating the dissolution of metal atoms, allowing for displaying the prominent durability during oxygen reduction process. Pt‐based intermetallic compounds have been considered promising electrocatalysts in the practical applications of fuel cells; however, the development of Pt‐based catalysts that meet performance targets of high activity, maximized stability, and low cost remains a huge challenge. Herein, an atomically ordered and low‐Pt intermetallic nitride (PtMn3N) catalyst are synthesized consisting of a strained Pt shell and PtMn3N core on carbon support via the KCl‐matrix protection strategy. The PtMn3N catalyst represents a high mass activity of 0.70 A mgPt−1 at 0.9 V and a specific activity degradation of 4.2% after 5000 potential cycles for the oxygen reduction reaction (ORR) in rotating disk electrode (RDE) testing, which substantially outperformed commercial Pt/C (0.25 A mgPt−1 and 17.4%). Density functional theory calculations reveal that the introduction of Mn elements to the Pt lattice is beneficial to produce appropriate compressive strain to weaken the binding energy of oxygen species and the introduction of N elements to promote the strong metal‐N interactions is conducive to alleviating the dissolution of metal atoms, allowing for displaying the prominent durability. This work provides an effective strategy of N‐doped Pt‐based intermetallic compounds to enhance the corrosion resistance of 3d transition metals and to enhance the ORR performance.

Optimizing the ORR performance of PtMnM ternary intermetallics by tuning the surface strain

Tuning Nanoparticle Structure and Surface Strain for Catalysis Optimization.

Anisotropic Strain Tuning of L10 Ternary Nanoparticles for Oxygen Reduction.

Tunable strain drives the activity enhancement for oxygen reduction reaction on Pd@Pt core-shell electrocatalysts

Anisotropic Strain Tuning Of L1(0) Ternary Nanoparticles For Oxygen Reduction

Enhancing Surface Strain of Intermetallic Fuel Cell Catalysts by Composition-Induced Phase Transition

Fine‐Tuning Intrinsic Strain in Penta‐Twinned Pt–Cu–Mn Nanoframes Boosts Oxygen Reduction Catalysis

Regulating the Surface Pt Coordination Environment in the PtN Overlayers on PtCuN Hollow Nanospheres for Efficient Oxygen Reduction Reaction

Phase engineering of Pt-Mn intermetallics for durable oxygen reduction reaction electrocatalysis

Synergistic Ni‐W Dimer Sites Induced Stable Compressive Strain for Boosting the Performance of Pt as Electrocatalyst for the Oxygen Reduction Reaction

Marriage of Ultralow Platinum and Single-Atom MnN 4 Moiety for Augmented ORR and HER Catalysis

Roles of Mo Surface Dopants in Enhancing the ORR Performance of Octahedral PtNi Nanoparticles.

Improving Oxygen Reduction Reaction Performance of Pt by a N-Doping Strategy and Inducing Tensile Strain of Nanoparticles

Unraveling the mechanism of ligands regulating electronic structure of MN4 sites with optimized ORR catalytic performance

Achieving Highly Durable Intermetallic PtMn3N Electrocatalyst via the Strong Metal‐N Bonds toward Oxygen Reduction Reaction

Highly Dispersed Cu Atoms Induce Alternating Surface Microstrain in PtCu Concave Octahedral Nanoparticles Accelerating Oxygen Reduction Reaction

Symmetry-Induced Regulation of Pt Strain Derived from Pt3 Ga Intermetallic for Boosting Oxygen Reduction Reaction.

Optimizing the Electronic Structure of Ordered Pt–Co–Ti Ternary Intermetallic Catalyst to Boost Acidic Oxygen Reduction

MoOy-Pt(CuNi)x Heterojunction Nanostructured Catalyst for Promoting the Oxygen Reduction Reaction Activity Property

L10‐PtCo and L12‐Pt3Co Intermetallics for Oxygen Reduction Reaction: the Influence of Composition and Structure on Properties

Enhancing Oxygen Reduction Activity Via Tailoring Microstrain in PdMo Nanoalloy Through Repetitive Hydrogen Absorption–Release