Polyaniline-Derived Carbon Heterostructure as Redox Mediator of Li 2 S Oxidation and Polysulfide Immobilizer for High-Performance Lithium–Sulfur Cathode
Hong Liu,Peng Zeng,Yongfang Li,Hao Yu,Manfang Chen,Sidra Jamil,Changqing Miao,Gairong Chen,Qi-Cheng Liu,Zhigao Luo,Xianyou Wang
DOI: https://doi.org/10.1021/acssuschemeng.0c06310
2020-10-23
Abstract:The merit of high energy density endows the lithium sulfide (Li<sub>2</sub>S)-based lithium–sulfur batteries (LSBs) as a promising candidate for next-generation energy storage batteries. In this work, Li<sub>2</sub>S is chemically anchored onto the surface of two-dimensional graphene oxide (GO), which is then tangled and connected by one-dimensional carbon nanotube (CNT) to promote electron transfer, and finally further embedded with PANI-derived carbon (PDC) to suppress a polysulfide shuttle. The deliberately designed carbon matrix offers a fast electron and ion transfer route, suitable surface area, void volume, and pore size for redox reactions and polysulfide confinement. Furthermore, PDC could synergistically immobilize polysulfides inside the cathode by means of chemisorption so as to restrain the shuttle effect in LSBs. Last but not least, PDC with a quinone-based structure could function as a redox mediator (RM) to facilitate Li<sub>2</sub>S oxidation with minimized polarization. Benefited from the aforementioned advantages, the as-fabricated Li<sub>2</sub>S-GO/CNT/PDC composite, which is coupled with a lithium metal as the anode, delivers initially a high specific capacity of 925 mAh g<sup>–1</sup> at 0.1 C and good retention capability of 550 mAh g<sup>–1</sup> after 400 cycles at 2 C. Therefore, the good electrochemical behavior of the Li<sub>2</sub>S-GO/CNT/PDC composite suggests its promising prospects for the commercial application of LSBs in high-energy storage devices.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c06310?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c06310</a>.Figure S1, Tafel slope analysis of Li<sub>2</sub>S-GO/CNT/PDC (red) and Li<sub>2</sub>S-GO/CNT (blue) for the first CV cycle; Figure S2, cycling performance of Li<sub>2</sub>S-GO/CNT/PDC with an areal loading of 3.1 mg cm<sup>–2</sup> at 0.2 C; Figure S3, FESEM images of the separators of the Li–S cells before and after cycling, the separator before cycling, the separator of Li<sub>2</sub>S-GO/CNT after cycling, and the separator of Li<sub>2</sub>S-GO/CNT/PDC after cycling; Figure S4, EIS spectra of Li<sub>2</sub>S-GO/CNT (blue) and Li<sub>2</sub>S-GO/CNT/PDC (red) after cycling; and Table S1, recent literature on the electrochemical performance of redox mediator-aided LSBs (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c06310/suppl_file/sc0c06310_si_001.pdf">PDF</a>)(<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c06310/suppl_file/sc0c06310_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology