Abstract:Undoped and Mn-doped ZnS nanocrystals were produced by the microwave-assisted solvothermal method and characterized by X-ray diffraction, photoluminescence spectroscopy and scanning electron microscopy with energy-dispersive X-ray spectroscopy. All samples have the cubic zinc blende structure with the lattice parameter in the range of a = 5.406–5.411 Å, and the average size of crystallites is in the range of 6–9 nm. These nanoparticles agglomerate and form large grains with an average size of up to 180 nm. The photoluminescence of the undoped ZnS sample shows a broad emission band located at 530 nm, attributed to the defects at the surface of nanoparticles. In all Mn-doped samples, the emission peak at 598 nm was observed assigned to the characteristic forbidden transition between excited ( 4 T 1 ) and ground ( 6 A 1 ) levels of Mn 2+ . Synchrotron radiation X-ray absorption spectroscopy at the Zn and Mn K-edges combined with reverse Monte Carlo (RMC) simulations based on the evolutionary algorithm confirms that manganese ions substitute zinc ions. However, the difference in the ion sizes ( R (Mn 2+ (IV)) = 0.66 Å and R (Zn 2+ (IV)) = 0.60 Å) is responsible for the larger interatomic distances Mn–S (2.40(2) Å) compared to Zn–S (2.33(2) Å). The static structural relaxations in ZnS:Mn nanoparticles are responsible for the large values of the mean-square displacements factors for Zn, S and Mn atoms obtained by RMC simulations.

Microwave-assisted synthesis and characterization of undoped and manganese doped zinc sulfide nanoparticles

Synthesis of Two-Dimensional Micron-Sized Single-Crystalline ZnS Thin Nanosheets and Their Photoluminescence Properties

Enhanced Photoluminescence and Characterization of Mn-Doped Zns Nanocrystallites Synthesized in Microemulsion

Studies of synthesis and optical properties of ZnS nanocrystals

Structure Characterization, Magnetic and Photoluminescence Properties of Mn Doped ZnS Nanocrystalline

Optical characterization of manganese-doped zinc sulfide nanoparticles synthesized in microemulsion

Paramagnetic nature of Mn doped ZnS nano particles in opto electronic device application

Microstructures and Luminescence Behaviors of Mn2+ Doped ZnS Nanoparticle Clusters with Different Core/shell Assembled Orders

Optical and magnetic properties of manganese-doped zinc sulfide nanoclusters

Luminescent Properties of ZnS∶Mn Nanoparticles Dependent on Doping Concentration

Examining the Effect of Cu and Mn Dopants on the Structure of Zinc Blende ZnS Nanopowders

Synthesis and Characterization of High-Quality Colloidal Mn2+-Doped Zns Nanoparticles

Continuous-Flow Synthesis of Zn1- xMnxS Nanoparticles at Ambient Conditions

Facile Synthesis Of Highly Luminescent Mn-Doped Zns Nanocrystals

Facile Hydrothermal Synthesis of Mn Doped ZnS Nanocrystals and Luminescence Properties Investigations

Experimental and Theoretical Study of the Mechanoluminescence of ZnS:Mn Nanoparticles

Facile Synthesis of Mn-doped ZnS Nanocrystals and Determination of Critical Temperature for Lattice Diffusion Process.

Colloidal manganese doped ZnS nanoplatelets and their optical properties

Structural and Optical Studies on Cr-Doped ZnS Nanoparticles Prepared by Flat Co-precipitation Method

Synthesis, Characterization and Magnetic Property Measurements of Zn1-Xmnxo Nanoparticles Via Vapour Phase Growth

Structural, Optical, and Electrical Properties of Cu-Doped ZnS Nanoparticles Prepared by Solid-State Reaction