Performance and durability studies of a catalyst-coated membrane containing a low-Ir-content Sr(Ti,Ir)O 3 anode for use in proton exchange membrane water electrolysis

Yukina Uchino,Takaya Ochiai,Atsushi Unemoto
DOI: https://doi.org/10.1016/j.ijhydene.2024.01.121
IF: 7.2
2024-01-18
International Journal of Hydrogen Energy
Abstract:Proton exchange membrane water electrolysis (PEMWE) is expected to be used in the large-scale green hydrogen production. Reducing the Ir content of the anode catalyst is desirable, as the availability of Ir is limited, thus increasing the cost of PEMWE. To reduce the Ir content, a perovskite-type Sr(Ti,Ir)O 3 is investigated. Characterization and activity studies in acid suggest that the composition realizing both high catalytic activity and low Ir concentration is SrTi 0.67 Ir 0.33 O 3 . Prototype catalyst-coated membranes (CCMs) containing SrTi 0.67 Ir 0.33 O 3 anodes are prepared. Regardless of the small Ir loading of 0.17 mg Ir cm −2 , high efficiencies of 86.4 % and 69.8 % are respectively observed at 1 and 2 A cm −2 , and 60 °C. Long durability of 2660 h is demonstrated at 1 A cm −2 and 60 °C. The post analyses of the CCMs suggest that collapse of the perovskite structure and dissolution of the constituent elements of SrTi 0.67 Ir 0.33 O 3 are factors causing degradation.
energy & fuels,electrochemistry,chemistry, physical
What problem does this paper attempt to address?