Ionic liquid-induced ultrathin and uniform N-doped carbon-wrapped T-Nb2O5 microsphere anode for high-performance lithium-ion battery

Rui-Xue Sun,Yang Yue,Xin-Feng Cheng,Ke Zhang,Su-Ying Jin,Guang-Yin Liu,Yu-Xin Fan,Yan Bao,Xiao-Di Liu

DOI: https://doi.org/10.1007/s12598-020-01681-1

IF: 6.318

2021-03-02

Rare Metals

Abstract:<span class="a-plus-plus abstract-section id-a-sec1"><p class="a-plus-plus">Orthorhombic-phase Nb<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub> (T-Nb<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub>) has been widely investigated as an intercalation anode material for Li-ion batteries due to the larger interplanar lattice spacing and high safety. However, its applications are limited by the intrinsic low electric conductivity. Herein, an ultrathin N-doped carbon-coating layer was constructed on porous T-Nb<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub> microspheres uniformly via a convenient thermal treatment method with ionic liquid as a carbon precursor. The synthesized T-Nb<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub>@N–C exhibits significantly enhanced rate capability (155.5 mAh·g<sup class="a-plus-plus">–1</sup> at 20C) than initial T-Nb<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub> (110.2 mAh·g<sup class="a-plus-plus">–1</sup> at 20C). Besides, T-Nb<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub>@N–C shows ultralong cycle life, with only a 0.02% decrease in the capacity per cycle at a high current density of 10C. The corresponding electrochemical tests show that the preferable rate capability of T-Nb<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub>@N–C electrode is attributed to the increased electronic conductivity and pseudocapacitance contribution induced by ultrathin surface N-doped carbon layer. On the other hand, the mesoporous structure of T-Nb<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub>@N–C ensures fast Li<sup class="a-plus-plus">+</sup> diffusion dynamics and electrolyte penetration. Furthermore, T-Nb<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub>@N–C also performs well in a LiNi<sub class="a-plus-plus">0.5</sub>Mn<sub class="a-plus-plus">0.3</sub>Co<sub class="a-plus-plus">0.2</sub>O<sub class="a-plus-plus">4</sub>||T-Nb<sub class="a-plus-plus">2</sub>O<sub class="a-plus-plus">5</sub>@N–C full cell. This work provides a facile method to construct integrated anode materials for potential applications in lithium-ion batteries.</p></span>

materials science, multidisciplinary,metallurgy & metallurgical engineering